Product obtained by polymerization of propylene in presence of complex organic metal catalysts. It incorporates increased long-term thermal stability, thermaloxidative degradation resistance when PP is produced, processed and PP-made articles are exploited, improved properties contributing to slipping and preventing from film layers sticking, improved rheology of melt. Application: extrusion flat-slot and tubular film. Technical requirements: TU 2211-136-05766801-2006 |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | |
| Apparent Density | 0.48 to 0.52 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 to 7.0 | g/10 min | ASTM D1238 |
| Ash Content | 0.025 to 0.050 | % | |
| Gel Content 1 | |||
| > 200.0 µm | 250 | pcs/m² | |
| 0.700 to 1.50 mm | 3.00 | pcs/m² | |
| 1.50 to 2.50 mm | 0.00 | pcs/m² | |
| > 2.50 mm | 0.00 | pcs/m² |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Thermal Creep Temperature 2 | 90 to 96 | °C | |
| Thermal-oxidative Deterioration (150°C) | 15.0 | day |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 82 to 95 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 31.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 9.0 | % | ASTM D638 |
| Flexural Modulus | 1250 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Vicat Softening Temperature 3 | 150 to 154 | °C |
| Note Message | |
|---|---|
| 1 . | p.4.8 TU 2211-136-05766801-2006 |
| 2 . | at load 0.46 H/mm² |
| 3 . | in liquid medium under force 10 H |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax PL806N | INDELPRO, S.A. de C.V. | PP Homopolymer | Pro-fax |
| NEFTEKHIM PP 9300M | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| Laser+® C 9921 (F65A) | DAK Americas LLC | PET | Laser+® |
| Leona™ 93G33 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |
| LEXAN™ FST9405 resin | SABIC Innovative Plastics | PC | LEXAN™ |