The matrix plastic of Kareline® PSMS is polystyrene. The fibre used is ECF bleached long fibre Nordic soft wood pulp (cellulose). The fibre content of Kareline® PSMS composites is normally 10-20 weight% (Kareline® PSMS9010, Kareline® PSMS8020). Customer tailor-made grades, e.g. with higher fibre content, are available.

Kareline® PSMS gives a very beautiful natural appearance to products in applications where no absolute mechanical properties are needed but where excellent surface quality and fascinating outlook are a desired property e.g. packaging of cosmetics or jewellery. Material has also very good dimensional stability in moulding and as a product.

Kareline® PSMS composites have a lot of good properties:

High rigidity

Excellent abrasion resistance

Pleasant feel of surface and beautiful natural surface appearance

Problem-free surface treatment

Good dimensional stability

General Information
Filler / Reinforcement	Wood Fiber
Features	Electrically Insulating Good Abrasion Resistance Good Chemical Resistance Good Dimensional Stability Good Weather Resistance High ESCR (Stress Crack Resist.) High Rigidity Laser Markable Machinable Outstanding Surface Finish Paintable Pleasing Surface Appearance Renewable Resource Content Thermally Insulating Ultrasonic Weldable
Uses	Cosmetic Packaging Packaging
Appearance	Light Brown
Forms	Pellets
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	1.15	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (200°C/10.0 kg)	2.96	cm³/10min	ISO 1133
Molding Shrinkage	0.50	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2400	MPa	ISO 527-2
Tensile Stress (Yield)	44.8	MPa	ISO 527-2
Tensile Strain (Yield)	2.2	%	ISO 527-2
Flexural Modulus	6000	MPa	ISO 178
Tensile Strength/Weight Ratio	39.0	MPa/g/cm³

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	1.6	kJ/m²	ISO 179

Thermal	Nominal Value	Unit
Continuous Use Temperature	-20.0 to 100	°C

Flammability	Nominal Value		Test Method
Flame Rating ¹	HB		UL 94

Injection	Nominal Value	Unit
Drying Temperature	80.0 to 100	°C
Drying Time	4.0 to 8.0	hr
Rear Temperature	200	°C
Middle Temperature	195	°C
Front Temperature	190	°C
Nozzle Temperature	180	°C
Processing (Melt) Temp	< 210	°C
Mold Temperature	20.0 to 50.0	°C
Injection Pressure	< 100	MPa

Note Message
1 .	23°C, 50%RH, 48h

Resin Grade	Manufacturer	Category	Trademark
Sindustris PBT TE5001D	Sincerity Australia Pty Ltd.	PC+PBT	Sindustris PBT
TAISOX 7140F	Formosa Plastics Corporation	EVA	TAISOX
KOCETAL® EL304BK	Kolon Plastics, Inc.	Acetal (POM) Copolymer	KOCETAL®
Latilub 66-10T K/10	LATI S.p.A.	Nylon 66	Latilub
LNP™ THERMOCOMP™ GF006 compound	SABIC Innovative Plastics	PSU	LNP™ THERMOCOMP™