NYCOA Polyamide 4014 HST
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Nycoa (Nylon Corporation of America) |
| Trademark: | NYCOA Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | X2XChY_NYCOA-Polyamide-4014-HST.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NYCOA 4014 HST is a 14% glass fiber reinforced, heat stabilized, and translucent Nylon 6 resin used for injection molding. This grade features outstanding stiffness and dimensional stability. NYCOA 4014 HST is available in UV stable, custom colors, and impact modified grades. It also has excellent chemical resistance to greases, oils, and other hydrocarbons. NYCOA 4014 HST has been formulated for see through storage tanks for automotive fluids. Typical applications include reservoir bottles for brake oil, transmission fluid, engine coolant, and power steering fluid. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.50 | % | ASTM D955 |
| Transverse flow | 0.80 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.1 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 5000 | MPa | ASTM D638 |
| Tensile Strength 2 | 120 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus 4 | 4830 | MPa | ASTM D790 |
| Flexural Strength 5 | 150 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 64 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 220 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 203 | °C | ASTM D648 |
| Melting Temperature | 221 | °C | DSC |
| Additional Information |
|---|
| The value listed as Melting Point DSC, was tested in accordance with ASTM D789. |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Adell PE KR-14 | Adell Plastics, Inc. | HDPE | Adell PE |
| AMTOPP CH18 | Inteplast Group | PP, Unspecified | AMTOPP |
| K-Bin Rigid PVC KBD-3045 | K-Bin, Inc. | PVC, Unspecified | K-Bin Rigid PVC |
| LNP™ THERMOCOMP™ ZF0049 compound | SABIC Innovative Plastics | PPE+PS | LNP™ THERMOCOMP™ |
| LEXAN™ LXS1210 resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |