Plasti-Paste® II
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | Smooth-On, Inc |
| Trademark: | Plasti-Paste® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | X1qgXY_Plasti-Paste-II.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
New Plasti-Paste® II is a two component fiber-filled resin that is designed for vertical surface application. This no-odor formulation is an improved version of our original Plasti-Paste® formula, and the cured product is different in the following ways: 1. Plasti-Paste II is now phthalate free. 2. Cured plastic can be painted (original Plasti Paste® can not) and 3. It is harder, more rigid with better heat resistance. Part A is a liquid and Part B is a paste. New Mix Ratio is 1A: 2B by volume (62A:100B by weight). Pot life is 10 minutes at room temperature depending on mass. Demold time (can be handled) is about 90 minutes at room temperature depending on mass. Full cure; 24 hours at room temperature. Cure time can be accelerated by applying heat. Mixed material holds a vertical surface without sagging and cures to a strong, durable and lightweight plastic. Liquid material can be pigmented with So-Strong® color tints from Smooth-On. This plastic can be used for creating themed environments or special effects, used as a "mother mold" material to reinforce rubber molds and a variety of other applications. This plastic is also a powerful adhesive and can be used as a repair material for a variety of industrial applications. Cured plastic can be sanded, machined and painted with acrylic enamel paints. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.998 | g/cm³ | ASTM D1475 |
| Specific Volume | 1.00 | cm³/g | ASTM D1475 |
| Viscosity | Paste | ASTM D2393 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Mixing Ratio | 62A:100B by weight 1A:2B by volume |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow | 0.50 | % | ASTM D2566 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 70 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1620 | MPa | ASTM D638 |
| Tensile Strength (Break) | 14.8 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.1 | % | ASTM D638 |
| Flexural Modulus | 1400 | MPa | ASTM D790 |
| Flexural Strength | 26.5 | MPa | ASTM D790 |
| Compressive Modulus | 432 | MPa | ASTM D695 |
| Compressive Strength | 34.3 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 54.4 | °C | ASTM D648 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Pot Life (23°C) | 10 | min | ASTM D2471 |
| Demold Time (23°C) | 90 | min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Unichem 7012 WHITE | Colorite Polymers | PVC, Unspecified | Unichem |
| ARK 2150-60A | Arkadia Plastics, Inc. | TPU-Polyester | ARK |
| APEX® 90-A482R-90-NT | Teknor Apex Company | PVC, Flexible | APEX® |
| Cheng Yu ML3435 | Cheng Yu Plastic Company Limited | PC | Cheng Yu |
| Laticonther 52/11 CP1/600 F3 | LATI S.p.A. | PP Homopolymer | Laticonther |