RIALBATCH H 02 S 60 TC
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | RIALTI Srl |
| Trademark: | RIALBATCH |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Wz9hzF_RIALBATCH-H-02-S-60-TC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Homopolymeric compound with high content of mixed mineral fillers; heat stabilized. Grade specific for extrusion. Highstiffness and thermo-stability; extremely contained dimensional shrinkage. Available in the version natural and colored as per sample. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.52 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.80 | % | |
| Flow | 0.80 | % | |
| Ash Content | 60 | % | ISO 3451 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Pressure Test (165°C) | Not Qualified | IEC 335 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 79 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/20 | ||
| Yield, 23°C | 20.0 | MPa | |
| Break, 23°C | 18.0 | MPa | |
| Tensile Strain | ISO 527-2/20 | ||
| Yield, 23°C | 1.5 | % | |
| Break, 23°C | 10 | % | |
| Flexural Modulus 1(23°C) | 4500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 33.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 35 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength (23°C) | 2.3 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 72.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 100 | °C | ISO 306/B50 |
| Ball Pressure Test (125°C) | Pass | IEC 335 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 3.0 | hr | |
| Melt Temperature | 220 to 250 | °C | |
| Die Temperature | 40.0 to 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ColorRx® PP2-0200RX | LTL Color Compounders, Inc. | PP Random Copolymer | ColorRx® |
| DJSilicone NE--C-2/NE-C-2U | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| Ecotan B F30 FM SB NAT | Soredi S.p.a. | Nylon 6 | Ecotan B |
| Hanwha Total PP HI831 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| LEXAN™ 4701R resin | SABIC Innovative Plastics | PPC | LEXAN™ |