Novodur® HD 15
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | INEOS Styrolution Group GmbH |
| Trademark: | Novodur® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WyHrOa_NovodurHD15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Novodur® HD 15 is an easily processable ABS grade with well-balanced mechanical properties and an exellent chemical and stress cracking resistance FEATURES
APPLICATIONS
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 15.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.40 - 0.70 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 1.0 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.22 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 102 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 38.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 2.5 | % | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 10 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 6.0 | kJ/m² | ISO 179 |
| 23°C | 14 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | 90 | kJ/m² | ISO 179 |
| 23°C | 170 | kJ/m² | ISO 179 |
| Notched Izod Impact | ISO 180/A | ||
| -30°C | 6.0 | kJ/m² | ISO 180/A |
| 23°C | 16 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1 | |||
| 0.45 MPa, annealed | 99.0 | °C | ISO 75-2/B |
| 1.8 MPa, annealed | 93.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 100 | °C | ISO 306/B50 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.17 | W/m/K | DIN 52612 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength (1.50 mm) | 37 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 2.90 | IEC 60250 | |
| 1 MHz | 2.80 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 4.8E-3 | IEC 60250 | |
| 1 MHz | 7.9E-3 | IEC 60250 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 230 - 260 | °C | |
| Mold Temperature | 30 - 80 | °C |
| Note Message | |
|---|---|
| 1 . | 4h/80°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Unichem 6812-02 | Colorite Polymers | PVC, Flexible | Unichem |
| 4POM® 9I15120 | 4Plas | Acetal (POM) Homopolymer | 4POM® |
| Argothane® 29300 | Argotec LLC | TPU, Unspecified | Argothane® |
| FRAGOM PR/721 | Crosspolimeri S.p.A. | Polyolefin, Unspecified | FRAGOM |
| Delene 5580 | Shanghai Lin Gen Rubber Materials Co., Ltd. | TPE | Delene |