DOMAMID® 66STZX
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | DOMO Engineering Plastics SPA |
| Trademark: | DOMAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WyAgRG_DOMAMID-66STZX.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 66, high impact resistance also at low temperature, for injection moulding. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.08 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1(23°C, 72 hr) | 1.0 to 1.5 | % | ISO 2577 |
| Water Absorption (Saturation, 23°C) | 5.5 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1900 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 50.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | > 50 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 2000 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 21 | kJ/m² | |
| 23°C | 60 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 70.0 | °C | ISO 75-2/A |
| Melting Temperature | 258 to 262 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Processing (Melt) Temp | 260 to 285 | °C | |
| Mold Temperature | 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50% RH |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sofprene T® 540200A55 | SO.F.TER. SPA | SBS | Sofprene T® |
| Wellamid® GB1430-N | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| APEX® 80-C440-C | Teknor Apex Company | PVC, Flexible | APEX® |
| Flexiblend® PP-1301 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PP+EPDM | Flexiblend® |
| LNP™ LUBRICOMP™ ZX05506 compound | SABIC Innovative Plastics | PPE+PS | LNP™ LUBRICOMP™ |