VALOX™ ENH3500 resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WwsAV5_VALOXENH3500resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unfilled PBT, Non-Brominated & Non-Chlorinated Flame Retardant |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 20.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 1.8 - 2.8 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 3150 | MPa | ASTM D638 |
| -- | 3200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 44.0 | MPa | ASTM D638 |
| Yield | 39.0 | MPa | ISO 527-2/50 |
| Fracture 4 | 42.0 | MPa | ASTM D638 |
| Fracture | 38.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 5 | 3.0 | % | ASTM D638 |
| Yield | 3.0 | % | ISO 527-2/50 |
| Fracture 6 | 10 | % | ASTM D638 |
| Fracture | 8.0 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 7 | 2750 | MPa | ASTM D790 |
| -- 8 | 2700 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 70.0 | MPa | ISO 178 |
| Yield, 50.0mm span 9 | 77.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 40 | J/m | ASTM D256 |
| -30°C 10 | 50 | kJ/m² | ISO 180/1A |
| 23°C 11 | 5.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 60.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 12 | 60.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 170 | °C | ISO 306/B120 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 120 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40.0 - 60.0 | °C | |
| Rear Temperature | 230 - 240 | °C | |
| Middle Temperature | 235 - 250 | °C | |
| Front Temperature | 240 - 260 | °C | |
| Nozzle Temperature | 230 - 255 | °C | |
| Processing (Melt) Temp | 245 - 260 | °C | |
| Mold Temperature | 40.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 5.0 mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | Type 1, 50mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 2949-70LG Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NYCOA Polyamide 3340 UV HS | Nycoa (Nylon Corporation of America) | Nylon+PP | NYCOA Polyamide |
| Armlen® PP SC 10.1 | Poly Plastic | PP, Unspecified | Armlen® |
| Hostacom HYP 376D 201104 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| Integra™ PC 5017 R | PolySource, LLC | PC | Integra™ |