NEXUS PC PC20NBR
| Category: | PC , Polycarbonate |
| Manufacturer: | Nexus Resin Group, LLC. |
| Trademark: | NEXUS PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Wwck1P_NEXUS-PC-PC20NBR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Molding Grade PC With Release |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 234 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 57.2 | MPa | ASTM D638 |
| Flexural Modulus | 2340 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 82.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 127 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 246 to 274 | °C | |
| Middle Temperature | 260 to 288 | °C | |
| Front Temperature | 274 to 302 | °C | |
| Nozzle Temperature | 274 to 302 | °C | |
| Processing (Melt) Temp | 274 to 302 | °C | |
| Mold Temperature | 71.1 to 98.9 | °C | |
| Back Pressure | 0.345 to 1.38 | MPa | |
| Screw Speed | 40 to 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9604-95 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TOTAL Polypropylene Lumicene® M 3382 MZ | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| NEXT REPROCESSED PC 143-300R | NEXT Specialty Resins, Inc. | PC | NEXT REPROCESSED |
| Geon™ Vinyl Flexible B6D00 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| MACOMASS PVC MM-PVC E 1570 | MACOMASS Verkaufs AG | PVC, Flexible | MACOMASS PVC |