Zenite® 6140L
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | Zenite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WwWtLc_Zenite-6140L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Zenite® 6140L is a 40% glass fiber reinforced and lubricated liquid crystal polymer for injection molding. It has excellent impact resistance and excellent heat deflection temperature. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.71 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.50 | % | |
| Flow | 0.050 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 17000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 130 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 1.1 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 16500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 190 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 15 | kJ/m² | |
| 23°C | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 20 | kJ/m² | |
| 23°C | 23 | kJ/m² | |
| Notched Izod Impact Strength (23°C) | 12 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 280 | °C | ISO 75-2/A |
| Melting Temperature 1 | 335 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 4.0E-6 | cm/cm/°C | |
| Transverse | 6.4E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 45 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 175 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.400 mm | V-0 | ||
| 1.50 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Processing (Melt) Temp | 350 to 360 | °C | |
| Mold Temperature | 40.0 to 150 | °C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® S 35F 100 NAT | Radici Plastics | Nylon 6 | Radilon® |
| SLOVALEN® PC 79 GF 20 | Plastcom | PP, Unspecified | SLOVALEN® |
| TOTAL Polypropylene PPR 6232 | TOTAL Refining & Chemicals | PP Random Copolymer | TOTAL Polypropylene |
| Daelim Po1y® PP-173 | DAELIM INDUSTRIAL CO., LTD. | PP Homopolymer | Daelim Po1y® |
| Dryflex® SE 85A201 | ELASTO | TPE | Dryflex® |