Order Products : sales@su-jiao.com
TECHNYL® A 548B V15 BLACK 23 N
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ww5k0B_TECHNYL-A-548B-V15-BLACK-23-N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYL® A 548B V15 Black 23 N is a copolyamide 6.6/6, reinforced with 15% of glass fibre, heat stabilized, impact modified, for blow moulding. This product is available in black color. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.20 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | Internal method | |||
| Vertical flow direction | 0.98 | -- | % | Internal method |
| Flow direction | 0.98 | -- | % | Internal method |
| Molding Shrinkage Isotropy | 1.00 | -- | Internal method |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 5200 | 3500 | MPa | ISO 527-2/1A |
| Tensile Stress (Break) | 100 | 60.0 | MPa | ISO 527-2/1A |
| Tensile Strain (Break) | 5.0 | 9.0 | % | ISO 527-2/1A |
| Flexural Modulus | 4100 | -- | MPa | ISO 178 |
| Flexural Stress | 130 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 11 | 20 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 68 | 80 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 13 | -- | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | 58 | -- | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 215 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 242 | -- | °C | ISO 11357-3 |
| Extrusion | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 8.0 | hr | |
| Suggested Max Moisture | 0.080 | % | |
| Cylinder Zone 1 Temp. | 240 - 260 | °C | |
| Cylinder Zone 3 Temp. | 245 - 265 | °C | |
| Adapter Temperature | 245 - 265 | °C | |
| Die Temperature | 250 - 270 | °C |
| Extrusion instructions |
|---|
| Head Temperature: 250 to 270°CBlow Molding Mold Temperature: 40 to 60°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ PP301 BLK | PolyOne Corporation | PP, Unspecified | Maxxam™ |
| Softell CA7469A | LyondellBasell Industries | Polyolefin, Unspecified | Softell |
| VICTREX® PEEK 151G | Victrex plc | PEEK | VICTREX® PEEK |
| TRIEL® 5359GP | Samyang Corporation | TPEE | TRIEL® |
| Iupilon® EGN2030R2 | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |