BMC 1901
| Category: | Alkyd , Alkyd |
| Manufacturer: | Bulk Molding Compounds, Inc. |
| Trademark: | BMC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WvtbXz_BMC-1901.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| BMC 1901 molding compound is a mineral filled, glass-fiber-reinforced alkyd compound suitable for compression transfer molding. It is a general purpose with medium impact strength and good overall electrical properties. Typical applications include switch components, relay bases, stack insulator s and as a formable insulating putty for motor construction and repair. BMC 1901 molding compound is produced in extruded form in a range of industrial colors. It is available in logs up to 12 inches in length or as precut slugs, of specific weigh, in diameters from 3/4" to 2 7/8". Within this range, smaller diameters are supplied as multiple extrusions and weight tolerances are plus or minus 5% up to a maximum of plus or minus 15 grams. This product is also available in the form of continuous, Round rope in diameters ranging from ¾" to 1 ¼". Diameters of ½" and 5/8", as well as selected flat rope shapes, are supplied at an additional charge. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.20 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 to 0.60 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.28 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Barcol Hardness | 70 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strength | 121 | MPa | ASTM D790 |
| Compressive Strength | 165 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 160 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 260 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 1 | 13 | kV/mm | ASTM D149 |
| Dielectric Constant (60 Hz) | 7.30 | ASTM D150 | |
| Dissipation Factor (60 Hz) | 0.040 | ASTM D150 | |
| Arc Resistance | 180 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 600 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.59 mm | HB | ||
| 3.18 mm | HB | ||
| 6.35 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 138 to 166 | °C |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vipel® K022-CNP-25 | AOC, L.L.C. | Vinyl Ester | Vipel® |
| ACRYLITE® Satinice ZD 23 | Evonik Cyro LLC | Acrylic (PMMA) | ACRYLITE® |
| ExxonMobil™ PP1055E2 | ExxonMobil Chemical | PP Homopolymer | ExxonMobil™ |
| Fluon® PTFE G190 | Asahi Glass Co., Ltd. | PTFE | Fluon® |
| OTECH PVC OW740 - Connector | OTECH Corporation | PVC, Unspecified | OTECH PVC |