Clariant PBT PBT-1700
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Clariant Corporation |
| Trademark: | Clariant PBT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Wvpz5l_Clariant-PBT-PBT-1700.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Clariant PBT PBT-1700 is a polybutene terephthalate (PBT) material,. This product is available in North America and is processed by injection molding. The main features of Clariant PBT PBT-1700 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.8 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.080 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| Class m | 86 | ASTM D785 | |
| Class r | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 53.8 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 45 | % | ASTM D638 |
| Flexural Modulus | 2620 | MPa | ASTM D790 |
| Flexural Strength | 69.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 48 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 149 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 71.1 | °C | ASTM D648 |
| Melting Temperature | 220 - 225 | °C | |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 18 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.794 mm | V-0 | UL 94 | |
| 1.59 mm | V-0 | UL 94 | |
| 3.18 mm | V-0 | UL 94 | |
| 6.35 mm | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 232 - 274 | °C | |
| Middle Temperature | 232 - 274 | °C | |
| Front Temperature | 232 - 274 | °C | |
| Processing (Melt) Temp | 232 - 246 | °C | |
| Melt Temperature (Aim) | 241 | °C | |
| Mold Temperature | 65.6 - 82.2 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 20 - 80 | rpm | |
| Cushion | 3.18 - 6.35 | mm |
| Injection instructions |
|---|
| Injection Pressure: Use minimum pressure to achieve 95% fill during the boost inj. pressure phase.Hold Pressure: 30% to 75% of injection pressure.Mold Temp. Target: 165°FScrew Speed Target: 50 RPM |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UBESTA XPA 9055 X2 | UBE Engineering Plastics, S.A. | Nylon 12 Elast | UBESTA |
| Ferro PP TPP10AN84BK | Ferro Corporation | PP, Unspecified | Ferro PP |
| Karina IVORY PVC COMPOUND 105911-35/ 1-BY-AC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 8205-75UV Grey 9592 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 3220-85 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |