HAIPLEN H50 T4
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | HAIPLEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Wuhl43_HAIPLEN-H50-T4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene homopolymer talcum filled 20%. Available: all colors, UV stabilized (L), heat stabilized (H), release agent (W), laser printable (LP), detergent stabilized (D). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.1 | % | |
| Across Flow | 1.1 | % | |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 30.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 40 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 2500 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 50.0 | MPa | ISO 178 |
| Break | 50.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 30 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 75.0 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 155 | °C | ASTM D1525, ISO 306/A50 2 1 |
| -- | 85.0 | °C | ASTM D1525, ISO 306/B50 3 2 |
| Ball Pressure Test (125°C) | Pass | VDE 0470 | |
| Melting Temperature | 165 | °C | ASTM D211, ISO 121 |
| CLTE - Flow | 6.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate (2.00 mm) | < 100 | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (1.60 mm) | 650 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 550 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 1.0 | hr | |
| Processing (Melt) Temp | 190 to 220 | °C | |
| Mold Temperature | 30.0 to 50.0 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 1 (10 N) |
| 2 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUMIKASUPER® LCP E6007AS | Sumitomo Chemical Co., Ltd. | LCP | SUMIKASUPER® LCP |
| Elastollan® S95AN | BASF Corp. Thermoplastic Polyurethanes | TPU-Polyester | Elastollan® |
| Epic Epoxy S7465 | Epic Resins | Epoxy | Epic Epoxy |
| Sylvin 3240-60 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LGE 321 | LG Polymers India Pvt. Ltd. | PS (EPS) | LGE |