Heramid® A GRI 7645 ECP1904
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Radici Plastics |
| Trademark: | Heramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Wu3RQY_Heramid-A-GRI-7645-ECP1904.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PA66 15% mineral filled injection moulding grade. Heat stabilized. Toughened. Grey colour. Post-industrial grade produced with selected polymers coming from polymerization, fibres and compounding plants. ISO 1043 : PA66-I MX15 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Recycled Content |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.21 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3500 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 70.0 | MPa | ISO 527-2/1A/5 |
| Nominal Tensile Strain at Break | 10 | % | ISO 527-2/1A/50 |
| Flexural Modulus 1 | 3200 | MPa | ISO 178 |
| Flexural Stress 2 | 110 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 80 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 80.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 90.0 | °C | ISO 306/B50 |
| Melting Temperature 3 | 265 | °C | ISO 11357 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80.0 | °C | |
| Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr | |
| Dew Point - Desiccant Dryer | < -20.0 | °C | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2000 R-4400 | RTP Company | PPSU | RTP |
| EUROPLEX® Film HC 0F045 | Evonik Industries AG | PVDF+PMMA | EUROPLEX® Film |
| 3M™ Dyneon™ PTFE Compound TF 8914 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| LEXAN™ HFD1433 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| Kepital® TE-23(FU2015) | KEP Americas | Acetal (POM) Copolymer | Kepital® |