LG ABS XR404
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | LG ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WtcBK9_LG-ABS-XR404.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description Heat Resistance Applications Electric & Electronic Housing (Frame etc), Automotives Interior & Exterior Housing (Garnish etc) |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 7.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 108 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 49.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 20 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2550 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 3.20 mm) | 78.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 69 | J/m | |
| -30°C, 6.40 mm | 59 | J/m | |
| 23°C, 3.20 mm | 220 | J/m | |
| 23°C, 6.40 mm | 200 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 108 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 100 | °C | |
| Vicat Softening Temperature | 109 | °C | ASTM D1525 5 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI Str | 60.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.5E+3 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.00 mm) | 33 | kV/mm | ASTM D149 |
| Arc Resistance | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) 6 | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.070 | % | |
| Rear Temperature | 180 to 200 | °C | |
| Middle Temperature | 200 to 220 | °C | |
| Front Temperature | 220 to 230 | °C | |
| Nozzle Temperature | 220 to 230 | °C | |
| Processing (Melt) Temp | 190 to 210 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Back Pressure | 0.981 to 2.94 | MPa |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 15 mm/min |
| 4 . | 15 mm/min |
| 5 . | Rate A (50°C/h), Loading 2 (50 N) |
| 6 . | Solution A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ FR PP 301 BLK 1284-11 S | PolyOne Corporation | PP, Unspecified | Maxxam™ FR |
| TULAMID® PA-SV20 | UCC Shchekinoazot | Nylon 6 | TULAMID® |
| ALTECH® PA66 A 2035/508 GF35 | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| Fainplast PVC GK 01450/R | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| ICORENE® N2215 | ICO Polymers EMEA, A Division of A. Schulman | LDPE | ICORENE® |