Lupoy® SG5009FA
| Category: | PC+ABS+Acrylic , Polycarbonate + ABS + Acrylic |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupoy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WtaRql_Lupoy-SG5009FA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lupoy®SG5009FA is a Polycarbonate ABS Acrylic (PMMA) (PC ABS Acrylic) material,. This product is available in North America, Latin America, Europe or Asia Pacific. The processing method is injection molding. Lupoy®The main features of the SG5009FA are:
Typical application areas include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.30 - 0.50 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Pencil Hardness 1 | F | ASTM D3363 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield, 3.20 mm) | 66.7 | MPa | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2790 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 3.20 mm) | 103 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 83 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 6.40 mm) | 94.0 | °C | ASTM D648 |
| RTI Elec | 80.0 | °C | UL 746 |
| RTI Imp | 80.0 | °C | UL 746 |
| RTI | 80.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.20 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 - 85.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Rear Temperature | 230 - 270 | °C | |
| Middle Temperature | 235 - 270 | °C | |
| Front Temperature | 235 - 270 | °C | |
| Nozzle Temperature | 235 - 270 | °C | |
| Processing (Melt) Temp | 245 - 270 | °C | |
| Mold Temperature | 90.0 - 120 | °C | |
| Back Pressure | 0.981 - 1.96 | MPa | |
| Screw Speed | 40 - 70 | rpm |
| Injection instructions |
|---|
| Minimum Moisture Content: 0.04% |
| Note Message | |
|---|---|
| 1 . | 500 g |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TITANLENE® LDF 201FG | Lotte Chemical Titan (M) Sdn. Bhd. | LDPE | TITANLENE® |
| Utomer T795A | Shanghai Utomer Material Science Co., Ltd. | TPU-Polyester | Utomer |
| Laprene® 830000551 | SO.F.TER. SPA | SEBS | Laprene® |
| Hylon® N1035HHR | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| PLANAC BT-1030-02 | TOYOBO America, Inc. | PBT | PLANAC |