RTP ESD C 1200 T-85A
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WtSWRR_RTP-ESD-C-1200-T-85A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ESD Protection - Electrically Conductive |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 1.0 - 1.5 | % | ASTM D955 |
| Moisture Content | 0.010 | % |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Static Decay 1 | sec | FTMS 101C 4046.1 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A, 10 seconds | 90 | ASTM D2240 | |
| Shaw D | 45 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 2(100% Strain, 3.18 mm) | 12.4 | MPa | ASTM D412 |
| Tensile Strength 3(Break, 3.20 mm) | 15.2 | MPa | ASTM D412 |
| Tensile Elongation 4(Break) | > 300 | % | ASTM D412 |
| Tear Strength 5 | 96.3 | kN/m | ASTM D624 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | No Break | ASTM D256 | |
| Unnotched Izod Impact (3.20 mm) | No Break | ASTM D4812 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | < 1.0E+6 | ohms | ASTM D257 |
| -- | < 1.0E+5 | ohms | ESD STM11.11 |
| Volume Resistivity | < 1.0E+3 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 107 | °C | |
| Drying Time | 6.0 | hr | |
| Dew Point | -17.8 | °C | |
| Processing (Melt) Temp | 185 - 218 | °C | |
| Mold Temperature | 37.8 - 60.0 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Injection instructions |
|---|
| Desiccant Type Dryer Required. |
| Note Message | |
|---|---|
| 1 . | MIL-PRF-81705D, 5kV to 50 V, 12% RH |
| 2 . | Mouth die C, 510mm/min |
| 3 . | C mold, 500 mm/min |
| 4 . | Mouth die C, 500 mm/min |
| 5 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROMID A 280 G4 | Taro Plast S.p.A. | Nylon 66 | TAROMID A |
| Wellamid® MR340 42H-NBK1 | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| Adsyl 7416 XCP | LyondellBasell Industries | Polyolefin, Unspecified | Adsyl |
| Hostalen PP H7350FLS 303064 | LyondellBasell Industries | PP Homopolymer | Hostalen PP |
| LNP™ LUBRICOMP™ KFP032 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |