Geon™ HTX 92052
| Category: | PVC Alloy , Polyvinyl Chloride Alloy |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Geon™ HTX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Wsmgqv_Geon-HTX-92052.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Geon™ HTX 92052 is a Polyvinyl Chloride Alloy (PVC Alloy) product. It can be processed by extrusion and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Typical application: Outdoor Applications. |
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
| PVC Cell Classification | 4-22224-53-0000 | ASTM D4216 | |
| PVC Cell Classification | 13255 | ASTM D1784 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2900 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 41.3 | MPa | ASTM D638 |
| Flexural Modulus | 2830 | MPa | ASTM D790 |
| Flexural Strength | 76.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Compression Molded) | 88 | J/m | ASTM D256A |
| Drop Impact Resistance | ASTM D4226 | ||
| 23°C 3 | 67.2 | J/cm | |
| 23°C 4 | 67.2 | J/cm |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 87.8 | °C | |
| 0.45 MPa, Annealed, 3.18 mm | 91.7 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 81.1 | °C | |
| 1.8 MPa, Annealed, 3.18 mm | 85.0 | °C | |
| CLTE - Flow | 6.7E-5 | cm/cm/°C | ASTM D696 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Ease of Sizing | Acceptable |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 182 to 193 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 5.1 mm/min |
| 2 . | Type I, 5.1 mm/min |
| 3 . | Procedure A, C.125 Dart |
| 4 . | Procedure B, C.125 Dart |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PROTEQ™ C24UST4 | Marplex Australia Pty. Ltd. | PP Copolymer | PROTEQ™ |
| WanBlend® WHT-HF9175 | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | WanBlend® |
| Eastar™ EB062 | Eastman Chemical Company | Copolyester | Eastar™ |
| RTP 399 X 143507 | RTP Company | PC | RTP |
| LNP™ COLORCOMP™ HX215HPC compound | SABIC Innovative Plastics | PBT | LNP™ COLORCOMP™ |