SCHULADUR® A MV 14 SHI FR 1
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULADUR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WsLtxe_SCHULADUR-A-MV-14-SHI-FR-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High impact flame retardant halogenated PBT compound; without PBDE; UL (f1) black + white |
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.37 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 5.00 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 44.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 4.0 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | 15 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 9.0 | kJ/m² | ISO 179/1eA |
| 23°C | 20 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 123 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 61.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 213 | °C | ISO 306/A50 |
| -- | 134 | °C | ISO 306/B50 |
| RTI Elec | UL 746 | ||
| 0.750 mm | 140 | °C | UL 746 |
| 1.50 mm | 140 | °C | UL 746 |
| RTI Imp | UL 746 | ||
| 0.750 mm | 110 | °C | UL 746 |
| 1.50 mm | 110 | °C | UL 746 |
| RTI | UL 746 | ||
| 0.750 mm | 130 | °C | UL 746 |
| 1.50 mm | 130 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 600 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | UL 746 | ||
| 0.750 mm | PLC 0 | UL 746 | |
| 1.50 mm | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | UL 746 | ||
| 0.750 mm | PLC 4 | UL 746 | |
| 1.50 mm | PLC 3 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate (2.00 mm, Self-Extinguishing) | 0.0 | mm/min | ISO 3795 |
| Flame Rating | UL 94, IEC 60695-11-10, -20 | ||
| 0.750 mm | V-0 | UL 94, IEC 60695-11-10, -20 | |
| 1.50 mm | V-0 5VB | UL 94, IEC 60695-11-10, -20 | |
| 3.00 mm | V-0 5VA | UL 94, IEC 60695-11-10, -20 | |
| 2.00 mm | 5VB | UL 94, IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.750 mm | 960 | °C | IEC 60695-2-12 |
| 1.50 mm | 960 | °C | IEC 60695-2-12 |
| 3.00 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.750 mm | 650 | °C | IEC 60695-2-13 |
| 1.50 mm | 650 | °C | IEC 60695-2-13 |
| 3.00 mm | 650 | °C | IEC 60695-2-13 |
| Oxygen Index | 26 | % | ISO 4589-2 |
| Additional Information |
|---|
| 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Toyolac® 500 322 | Toray Plastics (Malaysia) Sdn. Bhd. | ABS | Toyolac® |
| E-RIALFILL H 15 H 20 TD | RIALTI Srl | PP Homopolymer | E-RIALFILL |
| Escorene™ Ultra FL 00218 | ExxonMobil Chemical | EVA | Escorene™ Ultra |
| InnoTuf® HP-2140A | Innovative Polymers, Inc. | TSU-Ether | InnoTuf® |
| Petrothene® NA442051 | LyondellBasell Industries | LDPE | Petrothene® |