POTICON OA30

Category:	Acetal (POM) Copolymer , Acetal (POM) Copolymer
Manufacturer:	Otsuka Chemical Co., Ltd.
Trademark:	POTICON
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	WsFMyH_POTICONOA30.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

The Poticon series features a potassium titanate micro-filler compounded in thermoplastic resins to provide outstanding micro-reinforcement and dimensional stability. The excellent surface smoothness of these compounds limits friction toward opposing materials, reducing wear and allowing for greaseless applications. Moreover, as Poticon diminishes damage toward the mold and metal die and offers excellent recyclability, it also decreases processing costs.

Advantages

Microscopic reinforcement

Superior friction sliding and wear reduction

Excellent dimensional accuracy and surface smoothness

Highly recyclable

Applications

Automotive Parts (gears, bearings)

LED Reflectors

Watch Parts (gears, ground plane)

Camera (image stabilization parts)

Sliding Parts (gears, wheel bearing)

Camera Module Parts

Motor Parts (cog-wheels, bearings)

OA30 Property: High strength, High rigidity

General Information
Features	High Dimensional Stability Low friction coefficient Rigidity, high High strength Recyclable materials
Uses	LEDs Gear Application in Automobile Field Camera application Bearing
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.68	g/cm³	ASTM D792
Molding Shrinkage
Flow	0.70	%
Transverse flow	1.4	%
Water Absorption (Equilibrium)	0.20	%	ASTM D570

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (M-Scale)	90		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength	111	MPa	ASTM D638
Tensile Elongation (Break)	3.5	%	ASTM D638
Flexural Modulus	8800	MPa	ASTM D790
Flexural Strength	169	MPa	ASTM D790
Coefficient of Friction (vs. Steel - Dynamic)	0.28
Abrasion Loss
-- ¹	29.6	10^-3 mm³/N·km
of counterpart ²	0.00	10^-3 mm³/N·km

Thermal	Nominal Value	Unit	Test Method
Heat Distortion	153	°C	ASTM D648

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	44	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
CLTE - Flow	3.0E-5	cm/cm/°C	ASTM D696

Flammability	Nominal Value		Test Method
Flame Rating	HB		UL 94

Injection	Nominal Value	Unit
Processing (Melt) Temp	185 - 215	°C
Mold Temperature	60 - 100	°C
Injection Pressure	70.0 - 100	MPa

Note Message
1 .	Surface pressure: 1MPa
2 .	Slipping velocity: 0.3m/sec

Resin Grade	Manufacturer	Category	Trademark
Maxelast® P1970	Nantong Polymax Elastomer Technology, Co., Ltd	TPE	Maxelast®
SILVER® ABS 313NH	Guangdong Silver Age Sci & Tech. Co., Ltd	ABS	SILVER®
UBE Nylon 7034 B	UBE Engineering Plastics, S.A.	Nylon 612	UBE Nylon
VALOX™ VX4920 resin	SABIC Innovative Plastics Europe	PBT	VALOX™
Exxtral™ Performance Polyolefin CNR012	ExxonMobil Chemical	TPO	Exxtral™ Performance Polyolefin