Order Products : sales@su-jiao.com
PRL TP-G30
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ws1u1w_PRL-TP-G30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL TP-G30 is a Polybutylene Terephthalate (PBT) product filled with 30% glass fiber. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.52 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 8.0 to 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.60 to 0.90 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 117 | MPa | |
| Break, 3.18 mm | 117 | MPa | |
| Flexural Modulus (3.18 mm) | 7580 | MPa | ASTM D790 |
| Flexural Strength (Break, 3.18 mm) | 193 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 218 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 202 | °C | |
| RTI Elec | UL 746 | ||
| 1.50 mm | 75.0 | °C | |
| 3.00 mm | 75.0 | °C | |
| RTI Imp | UL 746 | ||
| 1.50 mm | 75.0 | °C | |
| 3.00 mm | 75.0 | °C | |
| RTI Str | UL 746 | ||
| 1.50 mm | 75.0 | °C | |
| 3.00 mm | 75.0 | °C |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Comparative Tracking Index (CTI) (1.50 mm) | PLC 1 | UL 746 | |
| High Amp Arc Ignition (HAI) | UL 746 | ||
| 1.50 mm | PLC 2 | ||
| 3.00 mm | PLC 2 | ||
| Hot-wire Ignition (HWI) | UL 746 | ||
| 1.50 mm | PLC 2 | ||
| 3.00 mm | PLC 1 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 116 to 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 238 to 254 | °C | |
| Middle Temperature | 243 to 260 | °C | |
| Front Temperature | 249 to 266 | °C | |
| Processing (Melt) Temp | 232 to 260 | °C | |
| Mold Temperature | 65.6 to 87.8 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Silamid® M15 | Roonamid a.s. | Nylon 6 | Silamid® |
| Kotex KGN-30MRA | Kotec Corporation | PC | Kotex |
| INELEC INX-STY-06167 | Infinity LTL Engineered Compounds | PS (GPPS) | INELEC |
| Karina IVORY PVC COMPOUND 853-35/ 1-E-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plaslube® PC-50/TF/13/SI/2 NAT | Techmer Engineered Solutions | PC | Plaslube® |