Borpact™ BC918CF
| Category: | PP, High Crystal , High Crystallinity Polypropylene |
| Manufacturer: | Borealis AG |
| Trademark: | Borpact™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Wrg9GN_Borpact-BC918CF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BC918CF is a heterophasic copolymer. BC918CF is a high crystalline copolymer film resin. This grade is suitable for the manufacturing of unoriented films on cast lines, conventional blown film lines with air cooling as well as roll stack process for thermoformable films/sheets. CAS-No. 9010-79-1 |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus 1(23°C, Injection Molded) | 1400 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-3 | ||
| MD : 50 µm | 1150 | MPa | |
| TD : 50 µm | 980 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 50 µm | 570 | % | |
| TD : Break, 50 µm | 530 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C, Injection Molded | 1.2 | kJ/m² | |
| 23°C, Injection Molded | 35 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) | 168 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°, 50.0 µm) | 95 | ASTM D2457 | |
| Haze (50.0 µm) | 4.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SFC4506 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| CompaDur® 121 black (019) | DimeLika Plast GmbH | PBT | CompaDur® |
| KOCETAL® TC304 | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| Hostacom PPU X9067HS C12470 | LyondellBasell Industries | PP Copolymer | Hostacom |
| ULTEM™ 2200 resin | SABIC Innovative Plastics | PEI | ULTEM™ |