NORYL™ NH6020 resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Wre2we_NORYLNH6020resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Noryl* NH6020 is an unfilled, injection moldable modified polyphenylene ether resin. Designed for high heat resistance and thin wall FR performance, this resin delivers a UL94 V0 rating at 0.8 mm and is also non-halogenated according to VDE/DIN 472 part 815. Noryl NH6020 has a HDT > of 120 deg C, pass the BPT @ 125 deg C, pass the GWIT 775 deg C @ 1, 2 and 3 mm, has the CTI value > 250 V and may be an excellent material candidate for unattended appliances components, where IEC 60335 applies. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 14 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 11.6 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.70 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.18 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.060 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2740 | MPa | ASTM D638 |
| -- | 2740 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 78.9 | MPa | ASTM D638 |
| Yield | 77.4 | MPa | ISO 527-2/50 |
| Fracture 3 | 67.6 | MPa | ASTM D638 |
| Fracture | 56.6 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 4.6 | % | ASTM D638 |
| Yield | 4.6 | % | ISO 527-2/50 |
| Fracture 5 | 6.1 | % | ASTM D638 |
| Fracture | 4.2 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 3020 | MPa | ASTM D790 |
| -- 7 | 2690 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 114 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 121 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 9.8 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 36 | J/m | ASTM D256 |
| 23°C | 49 | J/m | ASTM D256 |
| -30°C 10 | 5.4 | kJ/m² | ISO 180/1A |
| 23°C 11 | 8.1 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 18.4 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 125 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 12 | 125 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 150 | °C | ASTM D1525 13 |
| -- | 141 | °C | ISO 306/B50 |
| -- | 151 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 7.8E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 7.5E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 7.0E-6 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 7.8E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 110 | °C | UL 746 |
| RTI Imp | 105 | °C | UL 746 |
| RTI | 110 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.5E+16 - 4.2E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength (1.60 mm, in Oil) | 27 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 2.70 | IEC 60250 | |
| 60 Hz | 2.70 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 2.9E-3 | IEC 60250 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | PLC 2 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 1 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.75 mm, Testing by SABIC | V-0 | UL 94 | |
| 2.5 mm, Testing by SABIC | 5VB 5VA | UL 94 | |
| Glow Wire Flammability Index (1.0 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.0 mm | 825 | °C | IEC 60695-2-13 |
| 2.0 mm | 800 | °C | IEC 60695-2-13 |
| 3.0 mm | 800 | °C | IEC 60695-2-13 |
| Oxygen Index | 37 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 120 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Hopper Temperature | 80 - 100 | °C | |
| Rear Temperature | 260 - 280 | °C | |
| Middle Temperature | 280 - 300 | °C | |
| Front Temperature | 300 - 320 | °C | |
| Nozzle Temperature | 280 - 300 | °C | |
| Processing (Melt) Temp | 300 - 320 | °C | |
| Mold Temperature | 100 - 130 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mineralblend® PP-1850 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PP Copolymer | Mineralblend® |
| Telcar® TL-4001C | Teknor Apex Company | TPE | Telcar® |
| ASTALAC™ ABS X17 | Marplex Australia Pty. Ltd. | ABS | ASTALAC™ |
| KOCETAL® LW301 | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| Mediprene® 500534M | ELASTO | TPE | Mediprene® |