Zytel® FG70G30HSLR NC010
| Category: | Nylon 66 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WqXVbZ_ZytelFG70G30HSLRNC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% Glass Reinforced, Heat Stabilized, Hydrolysis Resistant, Polyamide 66 with Developed for Food Contact Applications |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.37 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 1.1 | -- | % | ISO 294-4 |
| Flow | 0.30 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C, 2.00mm | 6.0 | -- | % | ISO 62 |
| Balance, 23°C, 2.00mm, 50% RH | 1.9 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 10000 | 7200 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 195 | 130 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.3 | 5.0 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | |||
| 1 hr | -- | 6800 | MPa | ISO 899-1 |
| 1000 hr | -- | 5100 | MPa | ISO 899-1 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 10 | 10 | kJ/m² | ISO 179/1eA |
| 23°C | 13 | 15 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 70 | 72 | kJ/m² | ISO 179/1eU |
| 23°C | 82 | 92 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | |||
| -30°C | 12 | 10 | kJ/m² | ISO 180/1A |
| 23°C | 12 | 14 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 261 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 253 | -- | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 80.0 | 20.0 | °C | ISO 11357-2 |
| Vicat Softening Temperature | 250 | -- | °C | ISO 306/B50 |
| Melting Temperature 2 | 262 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow | 2.2E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.1E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Effective Thermal Diffusivity | 6.85E-8 | -- | m²/s |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| FMVSS Flammability | SE/B | -- | FMVSS 302 | |
| Fogging | ISO 6452 | |||
| F-value (refraction) | 95 | -- | % | ISO 6452 |
| G-value (condensate) | 3.0E-4 | -- | g | ISO 6452 |
| Fill Analysis | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Heat Capacity of Melt | 2290 | -- | J/kg/°C | |
| Thermal Conductivity of Melt | 0.21 | -- | W/m/K |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Emission of Organic Compounds | 6.00 | -- | µgC/g | VDA 277 |
| Odor | 4.50 | -- | VDA 270 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Melt Temperature, Optimum | 295 | °C | |
| Mold Temperature, Optimum | 100 | °C | |
| Drying Recommended | yes | ||
| Hold Pressure Time | 3.00 | s/mm | |
| Maximum Screw Tangential Speed | 200 | mm/sec |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | 1.0E+11 | ohms·cm | IEC 60093 |
| Dielectric Strength | 38 | 32 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 4.30 | 11.0 | IEC 60250 | |
| 1 MHz | 4.10 | 4.60 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 7.0E-3 | 0.46 | IEC 60250 | |
| 1 MHz | 0.015 | 0.065 | IEC 60250 | |
| Comparative Tracking Index | 450 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 3(1.00 mm) | 24 | -- | mm/min | ISO 3795 |
| Flame Rating | UL 94, IEC 60695-11-10, -20 | |||
| 0.75 mm | HB | -- | UL 94, IEC 60695-11-10, -20 | |
| 1.5 mm | HB | -- | UL 94, IEC 60695-11-10, -20 | |
| Oxygen Index | 24 | -- | % | ISO 4589-2 |
| Fill Analysis | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melt Density | 1.20 | -- | g/cm³ | |
| Ejection Temperature | 210 | -- | °C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time - Desiccant Dryer | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 285 - 305 | °C | |
| Mold Temperature | 50 - 90 | °C | |
| Holding Pressure | 50.0 - 100 | MPa |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| 3 . | FMVSS 302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1385 TFE 13 SI 2 | RTP Company | PPS | RTP |
| Sevrene® 3582-90A | Vi-Chem Corporation | TPE | Sevrene® |
| KIBIPOL® PR-1205 | CHI MEI CORPORATION | IIR | KIBIPOL® |
| LNP™ LUBRICOMP™ JZL012 compound | SABIC Innovative Plastics Europe | PESU | LNP™ LUBRICOMP™ |
| Hostacom TRC 333N G72862 | LyondellBasell Industries | PP Copolymer | Hostacom |