HAIPLEN H30 G3
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | HAIPLEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WqBWBD_HAIPLEN-H30-G3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene homopolymer glass fiber reinforced 15%. Available: all colors, UV stabilized (L), heat stabilized (H), laser printable (LP), detergent stabilized(D). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.00 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.50 to 0.70 | % | |
| Across Flow | 0.60 to 0.80 | % | |
| Water Absorption (23°C, 24 hr) | 0.10 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 35.0 | MPa | ASTM D638 |
| Yield | 35.0 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 10 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 3000 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 45 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 155 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 120 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 155 | °C | ASTM D1525, ISO 306/A 3 2 |
| -- | 115 | °C | ASTM D1525, ISO 306/B 4 3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | > 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (3.20 mm) | 650 | °C | IEC 60695-2-12 |
| Oxygen Index | 21 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 220 to 250 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | Type I |
| 2 . | Loading 1 (10 N) |
| 3 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® GS5073 | Teknor Apex Asia Pacific PTE. LTD. | TPE | Telcar® |
| MTEGRITY™ PS High Impact IS200 | M. Holland Company | PS (HIPS) | MTEGRITY™ PS High Impact |
| THERMOLAST® K TC4GPN (Series: GP/FG) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Diamond ABS 3501 GF-20 | Network Polymers, Inc. | ABS | Diamond ABS |
| Karina CLEAR PVC COMPOUND E-85/269-K-AT-IS-SI | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |