Leona™ FG170
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | Leona™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WpkDoG_Leona-FG170.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Leona™ FG170 is a Polyamide 66 (Nylon 66) product filled with glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Typical application: Electrical/Electronic Applications. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.48 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 1.0 | -- | % | |
| Flow | 0.60 | -- | % | |
| Water Absorption | ||||
| Saturation, 23°C | -- | 1.2 | % | |
| Equilibrium, 23°C, 50% RH | -- | 1.2 | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (M-Scale) | 95 | 55 | ASTM D785, ISO 2039-2 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 7500 | 5700 | MPa | ISO 527-2 |
| Tensile Stress | ||||
| Break, 23°C | 131 | 100 | MPa | ISO 527-2 |
| -- | 132 | 108 | MPa | ASTM D638 |
| Tensile Elongation | ||||
| Break | 2.5 | 2.7 | % | ASTM D638 |
| Break, 23°C | 2.5 | 3.5 | % | ISO 527-2 |
| Flexural Modulus | ||||
| -- | 6400 | 4900 | MPa | ASTM D790 |
| 23°C | 7500 | 4700 | MPa | ISO 178 |
| Flexural Strength | ||||
| -- | 191 | 152 | MPa | ASTM D790 |
| 23°C | 188 | 146 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles) | -- | 24.0 | mg | ASTM D1044 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 6.0 | 5.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 44 | 45 | kJ/m² | ISO 179 |
| Notched Izod Impact | 49 | 59 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed | 255 | -- | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 256 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 248 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 240 | -- | °C | ISO 75-2/A |
| CLTE - Flow | 3.0E-5 | -- | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | -- | ohms | ASTM D257, IEC 60093 |
| Volume Resistivity | ||||
| -- | 1.0E+15 | -- | ohms·cm | ASTM D257 |
| 23°C | 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength | 27 | -- | kV/mm | ASTM D149, IEC 60243-1 |
| Comparative Tracking Index (3.00 mm) | 200 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.750 mm) | V-0 | -- | UL 94 | |
| Glow Wire Flammability Index (3.00 mm) | 960 | -- | °C | IEC 60695-2-12 |
| Oxygen Index | 38 | -- | % | ASTM D2863 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radiflam® A RV300AE 984 C GRI | Radici Plastics | Nylon 66 | Radiflam® |
| NEOPLAST 243 HOFR | Zylog Plastalloys | TPV | NEOPLAST |
| Fainplast PVC CRKA 87 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| OXNILON 66 30CF 15PTFE | Oxford Polymers | Nylon 66 | OXNILON 66 |
| Braskem PE LDI2020 | Braskem IDESA | LDPE | Braskem PE |