LNP™ LUBRICOMP™ OX90351 compound
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Wpa1EW_LNP-LUBRICOMP-OX90351-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* OX90351 is a compound based on Polyphenylene Sulfide resin containing Proprietary Filler(s). Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound PDX-O-90351 Product reorder name: OX90351 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.67 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.20 | % | ASTM D955 |
| Across Flow : 24 hr | 0.60 | % | ASTM D955, ISO 294-4 |
| Flow : 24 hr | 0.22 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.010 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.53 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 10300 | MPa | ASTM D638 |
| -- | 9720 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 100 | MPa | ASTM D638 |
| Break | 96.0 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 1.5 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 9170 | MPa | ASTM D790 |
| -- | 9380 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 153 | MPa | ASTM D790 |
| -- | 154 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 53 | J/m | ASTM D256 |
| 23°C 2 | 6.4 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 380 | J/m | ASTM D4812 |
| 23°C 3 | 20 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 2.60 | J | ASTM D3763 |
| -- | 2.45 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 261 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 260 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 304 to 316 | °C | |
| Middle Temperature | 321 to 332 | °C | |
| Front Temperature | 332 to 343 | °C | |
| Processing (Melt) Temp | 316 to 321 | °C | |
| Mold Temperature | 138 to 166 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ENVIROPLAS® ENV00-NC680 | ENVIROPLAS®, Inc. | ABS | ENVIROPLAS® |
| HANWHA LDPE 5318 | Hanwha Chemical | LDPE | HANWHA LDPE |
| Hylon® N1013THL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| Kumho KNB 3345 | Korea Kumho Petrochemical Co., Ltd. | NBR | Kumho KNB |
| Plaslube® HTN 01400 BK | Techmer Engineered Solutions | Nylon, Unspecified | Plaslube® |