SEETEC PP R3450
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | SEETEC PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WogVHP_SEETEC-PP-R3450.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Seetec R3450 is a polypropylene-ethylene random copolymer designed for the production of cast films. It has a good clarity due to the optimum content of ethylene and offers optimum balance between optical properties and physical strength. It is suitable for the skin layer of co-extruded cast film in food packaging or semi retort pouch being required high slip and medium heat seal temperature. SEETEC R3450 meets the FDA requirement in the code of Federal Regulations in 21 CFR 177.1520 and EU Directive 10/2011 for food contact. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 82 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 25.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | > 500 | % | ASTM D638 |
| Flexural Modulus | 900 | MPa | ASTM D790 |
| Coefficient of Friction (Static, Cast Film) | < 0.20 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 30 µm, Cast Film | 43.1 | MPa | |
| TD : Break, 30 µm, Cast Film | 33.3 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 30 µm, Cast Film | > 500 | % | |
| TD : Break, 30 µm, Cast Film | > 500 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 49 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 80.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 134 | °C | ASTM D1525 3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (30.0 µm, Cast Film) | 132 | ASTM D2457 | |
| Haze (30.0 µm, Cast Film) | 1.5 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Seal Temperature 4 | 130 | °C | Internal Method |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | Loading 1 (10 N) |
| 4 . | >1 kgf |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RANPELEN J-560S | Lotte Chemical Corporation | PP Random Copolymer | RANPELEN |
| RheTech Thermoplastic Polyolefin FT3080-47UV | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| Viprene™ P80A-22U-NAT | Alliance Polymers & Services | TPV | Viprene™ |
| Adell Polyamide AS-40 | Adell Plastics, Inc. | Nylon 66 | Adell Polyamide |
| Lucobit 1210 | Lucobit AG | PE Copolymer | Lucobit |