LNP™ LUBRICOMP™ WFL34H compound
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WneLhB_LNP-LUBRICOMP-WFL34H-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* WFL34H is a compound based on PBT resin containing 20% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant, Healthcare. Also known as: LNP* LUBRICOMP* Compound WFL-4034 HC Product reorder name: WFL34H |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.59 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.40 to 0.70 | % | |
| Across Flow : 24 hr | 0.90 to 2.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.050 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.070 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 8750 | MPa | ASTM D638 |
| -- | 8460 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 123 | MPa | ASTM D638 |
| Yield | 121 | MPa | ISO 527-2/5 |
| Break | 123 | MPa | ASTM D638 |
| Break | 121 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 3 | 2.8 | % | ASTM D638 |
| Yield | 2.7 | % | ISO 527-2/50 |
| Break | 2.8 | % | ASTM D638 |
| Break | 2.7 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- | 6840 | MPa | ASTM D790 |
| -- 4 | 7510 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 176 | MPa | ASTM D790 |
| -- | 182 | MPa | ISO 178 |
| Yield, 50.0 mm Span 5 | 177 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.48 | ||
| vs. Itself - Static | 0.47 | ||
| Wear Factor - Washer | 35.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 88 | J/m | ASTM D256 |
| 23°C 6 | 9.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 820 | J/m | ASTM D4812 |
| 23°C 7 | 46 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 9.60 | J | ASTM D3763 |
| -- | 3.20 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 223 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 8 | 223 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 213 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 9 | 209 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 221 to 232 | °C | |
| Middle Temperature | 243 to 254 | °C | |
| Front Temperature | 260 to 271 | °C | |
| Processing (Melt) Temp | 238 to 266 | °C | |
| Mold Temperature | 82.2 to 98.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 80*10*4 |
| 7 . | 80*10*3 |
| 8 . | 80*10*4 mm |
| 9 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRIBIT® LM1503 | Samyang Corporation | PBT | TRIBIT® |
| Adell Polyolefin ZS-30 | Adell Plastics, Inc. | Polyolefin, Unspecified | Adell Polyolefin |
| EcolGreen EGP-220 | EcolBiotech Co., Ltd | PLA | EcolGreen |
| EpoxAcast® 650 | Smooth-On, Inc | Epoxy | EpoxAcast® |
| POLYCOMPO PP B221WA | POLYCOMPO Co.,Ltd. | PP, Unspecified | POLYCOMPO PP |