Estane® 2103-90A TPU
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Estane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WnTAeb_Estane-2103-90A-TPU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
2103-90A is a thermoplastic polyurethane elastomer. Feature: Low compression set |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/8.7 kg) | 23 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 1.60 mm | 0.70 to 0.80 | % | |
| Across Flow : 1.60 mm | 0.70 to 0.80 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 75.8 | MPa | ASTM D790 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 10.0 | mg | ASTM D1044 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 50% Strain | 76.0 | MPa | |
| 100% Strain | 11.2 | MPa | |
| 300% Strain | 24.8 | MPa | |
| Tensile Strength (Break) | 44.8 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 450 | % | ASTM D412 |
| Elongation Set After Break | 30 | % | ASTM D412 |
| Tear Strength 1 | 133 | kN/m | ASTM D624 |
| Compression Set | ASTM D395B | ||
| 25°C, 22 hr | 25 | % | |
| 70°C, 22 hr | 28 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -25.0 | °C | DSC |
| Vicat Softening Temperature | 107 | °C | ASTM D1525 |
| CLTE - Flow | 1.5E-4 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 88.0 to 104 | °C | |
| Processing (Melt) Temp | 204 to 221 | °C | |
| Mold Temperature | 16.0 to 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | Die C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Yanshan PE 1C5A | SINOPEC Beijing Yanshan Petrochemical | LDPE | Yanshan PE |
| Gebalon 35-141 HI | geba Kunststoffcompounds GmbH | PC | Gebalon |
| LNP™ LUBRICOMP™ DP003EH compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |
| Plexiglas® V920 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Plexiglas® |
| POFEX 8200EP80M | POLYROCKS CHEMICAL CO., LTD | TPE | POFEX |