TIPELIN® 6300B
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | MOL Petrochemicals Co. Ltd. |
| Trademark: | TIPELIN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Wn9kpS_TIPELIN-6300B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TIPELIN 6300B is a high density bimodal polyethylene copolymer (with butene-1 as comonomer) intended for blow moulding of products with high stiffness and excellent environmental stress crack resistance (ESCR). The grade contains antioxidant and acid scavenger. TIPELIN 6300B is recommended for bottles and containers up to 10 litre capacity for detergents, household chemicals and for blow moulded products for packaging of aggressive industrial chemicals bounded to UN certificates. It is suitable for corrugated pipes too TIPELIN 6300B is suitable for food contact and for manufacturing of pharmaceutical packing products. The product complies with Food Contact and Pharmaceutical Regulations. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.954 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.30 | g/10 min | |
| 190°C/21.6 kg | 30 | g/10 min | |
| 190°C/5.0 kg | 1.3 | g/10 min | |
| Environmental Stress-Cracking Resistance (10% Igepal CO-630, F50) | 700 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 65 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 32.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 11 | % | |
| Break | 1300 | % | |
| Flexural Modulus | 1550 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 9.0 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 126 | °C | ISO 306/A120 |
| Oxidation Induction Time (200°C) | 32 | min | EN 728 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 to 165 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polytron® A35B01 | Polyram Ram-On Industries | Nylon 66 | Polytron® |
| TUFNYL® RGF 30 FRO GREY | SRF Ltd. | Nylon 66 | TUFNYL® |
| XENOY™ X4820 resin | SABIC Innovative Plastics | PC+PBT | XENOY™ |
| NOVAPOL® LF-Y320 Series | NOVA Chemicals | LDPE | NOVAPOL® |
| MACOMASS PP MM-PP HK 82 | MACOMASS Verkaufs AG | PP Homopolymer | MACOMASS PP |