Anjacom® R195-H/GF30
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | Almaak International GmbH |
| Trademark: | Anjacom® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WmifF5_Anjacom-R195-H-GF30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Anjacom® R195-H/GF30 is a Polyamide 66/6 Copolymer (Nylon 66/6) material filled with 30% glass fiber. It is available in Europe for injection molding. Important attributes of Anjacom® R195-H/GF30 are:
Typical application of Anjacom® R195-H/GF30: Automotive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.36 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.80 to 1.3 | % | |
| Flow | 0.30 to 0.60 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 5.8 | % | |
| Equilibrium, 23°C, 50% RH | 2.1 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8400 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 125 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.7 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 48 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 225 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 215 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 220 | °C | ISO 306/B50 |
| Melting Temperature (DSC) 1 | 245 | °C | Internal Method |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 10 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Processing (Melt) Temp | 275 to 300 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | Kofler |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirathane™ M80 | Miracll Chemicals Co., Ltd. | TPU-Polyether | Mirathane™ |
| Sylvin 916V0 Black | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| Argothane® ST-6050 | Argotec LLC | TPU, Unspecified | Argothane® |
| COSMOTHENE® EVA H2181 | TPC, The Polyolefin Company (Singapore) Pte Ltd | EVA | COSMOTHENE® EVA |
| Innothane® IE-8000 | Innovative Polymers, Inc. | TSU | Innothane® |