FORMULA P ELAN 3003 UV
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Putsch Kunststoffe GmbH |
| Trademark: | FORMULA P |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Wmg0uG_FORMULA-P-ELAN-3003-UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FORMULA P ELAN 3003 UV is a polypropylene product,. It is available in Europe. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.5 - 1.8 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 18.0 | MPa | ISO 527-2 |
| Fracture | 17.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 400 | % | ISO 527-2 |
| Flexural Modulus | 900 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 37.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180 | ||
| -20°C | 7.0 | kJ/m² | ISO 180 |
| 23°C | 35 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 58.0 | °C | ISO 306/B |
| Additional Information |
|---|
| Tensile Strength, ISO 527: 18 MPa |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 200 - 230 | °C | |
| Mold Temperature | 20.0 - 40.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Monprene® MP-2150 | Teknor Apex Company | TPE | Monprene® |
| Andur 9000 AP/Curene® 442 | Anderson Development Company | PUR-Ether/TDI | Andur |
| Elvaloy® AC 1820 | DuPont Packaging & Industrial Polymers | EMA | Elvaloy® |
| LUVOCOM® PA66/TF/40 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| Sylvin 7844-90C Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |