VALOX™ VX5022 resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WmKAMV_VALOX-VX5022-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| VALOX VX5022 is a 20% glass fibre reinforced PBT+PC blend with low warpage characteristics. This grade is 5021 with reduced warpage. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 250°C/2.16 kg | 16 | g/10 min | |
| 265°C/5.0 kg | 50 | g/10 min | |
| 266°C/5.0 kg | 50 | g/10 min | |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 250°C/2.16 kg | 13.0 | cm³/10min | |
| 250°C/5.0 kg | 28.0 | cm³/10min | |
| 265°C/5.0 kg | 40.0 | cm³/10min | |
| Molding Shrinkage | Internal Method | ||
| Flow 1 | 0.30 to 0.80 | % | |
| Flow : 3.20 mm | 0.30 to 0.50 | % | |
| Across Flow 2 | 0.50 to 0.90 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.10 | % | |
| Equilibrium, 23°C, 50% RH | 0.060 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 122 | ISO 2039-2 | |
| Ball Indentation Hardness (H 358/30) | 205 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 3 | 7300 | MPa | ASTM D638 |
| -- | 7100 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 4 | 125 | MPa | ASTM D638 |
| Yield | 110 | MPa | ISO 527-2/5 |
| Break 5 | 125 | MPa | ASTM D638 |
| Break | 110 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 6 | 3.0 | % | ASTM D638 |
| Yield | 3.0 | % | ISO 527-2/5 |
| Break 7 | 3.0 | % | ASTM D638 |
| Break | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 8 | 5800 | MPa | ASTM D790 |
| -- 9 | 6300 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 150 | MPa | ISO 178 |
| Yield, 50.0 mm Span 10 | 145 | MPa | ASTM D790 |
| Flexural Strain at Break 11 | 3.0 | % | ISO 178 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Filler Content | 20 | % | ASTM D229 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30°C 12 | 5.5 | kJ/m² | ISO 179/1eA |
| -30°C | 9.0 | kJ/m² | ISO 179/2C |
| 23°C 13 | 6.5 | kJ/m² | ISO 179/1eA |
| 23°C | 9.0 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength | |||
| -30°C 14 | 40 | kJ/m² | ISO 179/1eU |
| -30°C | 50 | kJ/m² | ISO 179/2U |
| 23°C 15 | 40 | kJ/m² | ISO 179/1eU |
| 23°C | 55 | kJ/m² | ISO 179/2U |
| Notched Izod Impact | |||
| -30°C | 80 | J/m | ASTM D256 |
| 0°C | 80 | J/m | ASTM D256 |
| 23°C | 80 | J/m | ASTM D256 |
| -30°C 16 | 6.0 | kJ/m² | ISO 180/1A |
| 0°C 17 | 7.0 | kJ/m² | ISO 180/1A |
| 23°C 18 | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| -30°C | 650 | J/m | ASTM D4812 |
| 23°C | 650 | J/m | ASTM D4812 |
| -30°C 19 | 35 | kJ/m² | ISO 180/1U |
| 23°C 20 | 40 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Total Energy) | 65.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 180 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 21 | 180 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 120 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 22 | 120 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 200 | °C | ASTM D1525, ISO 306/A50 12 23 |
| -- | 145 | °C | ASTM D1525, ISO 306/B50, ISO 306/B120 24 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE | |||
| Flow : -40 to 40°C | 4.0E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 2.5E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : 23 to 60°C | 4.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : 23 to 80°C | 4.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : 23 to 150°C | 2.4E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 1.0E-4 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 6.9E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : 23 to 60°C | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Transverse : 23 to 80°C | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Transverse : 23 to 150°C | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | ASTM D149, IEC 60243-1 | ||
| 0.800 mm, in Oil | 31 | kV/mm | |
| 1.60 mm, in Oil | 28 | kV/mm | |
| 3.20 mm, in Oil | 16 | kV/mm | |
| Dielectric Constant | |||
| 1 MHz | 3.30 | ASTM D150, IEC 60250 | |
| 50 Hz | 3.10 | IEC 60250 | |
| 60 Hz | 3.10 | IEC 60250 | |
| 100 Hz | 3.30 | IEC 60250 | |
| Dissipation Factor | |||
| 1 MHz | 0.014 | ASTM D150, IEC 60250 | |
| 50 Hz | 1.0E-3 | IEC 60250 | |
| 60 Hz | 1.0E-3 | IEC 60250 | |
| 100 Hz | 1.0E-3 | IEC 60250 | |
| Comparative Tracking Index | IEC 60112 | ||
| -- | 200 | V | |
| Solution B | 100 | V | |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm, Testing by SABIC) | HB | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 750 | °C | |
| 2.00 mm | 850 | °C | |
| Oxygen Index | 23 | % | ISO 4589-2 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (260°C, 1500 sec^-1) | 215 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40.0 to 60.0 | °C | |
| Rear Temperature | 230 to 245 | °C | |
| Middle Temperature | 240 to 255 | °C | |
| Front Temperature | 245 to 265 | °C | |
| Nozzle Temperature | 240 to 260 | °C | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 40.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | Tensile Bar |
| 3 . | 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | Type I, 5.0 mm/min |
| 7 . | Type I, 5.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 2.0 mm/min |
| 10 . | 1.3 mm/min |
| 11 . | 2 mm/min |
| 12 . | 80*10*4 sp=62mm |
| 13 . | 80*10*4 sp=62mm |
| 14 . | 80*10*4 sp=62mm |
| 15 . | 80*10*4 sp=62mm |
| 16 . | 80*10*4 |
| 17 . | 80*10*4 |
| 18 . | 80*10*4 |
| 19 . | 80*10*4 |
| 20 . | 80*10*4 |
| 21 . | 80*10*4 mm |
| 22 . | 80*10*4 mm |
| 23 . | Rate A (50°C/h), Loading 2 (50 N) |
| 24 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 D | RTP Company | Nylon 612 | RTP |
| PPR PPCO04 | Premier Plastic Resins, Inc. | PP Copolymer | PPR |
| RTP PP 40 GF UV | RTP Company | PP, Unspecified | RTP |
| EZPrene 9555A SHF | ENPLAST Americas, a Ravago Group Company | TPV | EZPrene |
| Hylex® P1017FRMA | Ravago Manufacturing Americas, LLC | PC | Hylex® |