LNP™ LUBRICOMP™ UFL269SA compound
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WlG1tD_LNPLUBRICOMPUFL269SAcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP UFL269SA is a compound based on Polyphthalamide resin containing Glass Fiber, PTFE, Flame Retardant. Added features of this material include: Internally Lubricated, Heat Stabilized, Flame Retardant. Also known as: LNP* LUBRICOMP* Compound UFL-4026 A FR HS Product reorder name: UFL269SA |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.71 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 0.20 - 0.40 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.70 - 0.90 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 13700 | MPa | ASTM D638 |
| Tensile Strength (Break) | 163 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.7 | % | ASTM D638 |
| Flexural Modulus | 12800 | MPa | ASTM D790 |
| Flexural Strength | 228 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.47 | ASTM D3702 Modified | |
| With Self-Static | 0.38 | ASTM D3702 Modified | |
| Wear Factor - Washer | 85.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 85 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 460 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 273 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, Testing by SABIC) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene HP521-229UV | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| Ultramid® B3GM35 BK60564 | BASF Corporation | Nylon 6 | Ultramid® |
| Carbotex K-50UVR | Kotec Corporation | PC | Carbotex |
| KumhoSunny ABS 730EM | Shanghai KumhoSunny Plastics Co., Ltd. | ABS | KumhoSunny ABS |
| Sylvin 802-88 UV Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |