Tribocomp® PA66 LGF30 N9 PTFE 15% MoS 0.5% Datasheet,Nylon 66,Solvay Specialty Polymers-SHANGHAI SUSHENG

Message
Tribocomp® PA66 LGF30 N9 PTFE 15% MoS 0.5%, is a 30% long glass fiber reinforced high-flow PA 6.6 with a pellet length of 9mm and contains 15% PTFE and 0.5% MoS2. It can easily be processed on most injection molding machines.

General Information
Filler / Reinforcement	PTFE fiber, 15% filler by weight Long glass fiber, 30% filler by weight
Forms	Particle

Physical	Dry	Conditioned	Unit	Test Method
Density	1.50	--	g/cm³	ISO 1183
shrinkage- Flow	0.40	--	%	ISO 294-4
Water Absorption (Equilibrium, 23°C, 50% RH)	1.4	--	%	ISO 62

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus				ISO 527-2
23°C	10500	7900	MPa	ISO 527-2
90°C	7100	--	MPa	ISO 527-2
120°C	5500	--	MPa	ISO 527-2
Tensile Stress				ISO 527-2
Yield, 23°C	200	125	MPa	ISO 527-2
Yield, 90°C	130	--	MPa	ISO 527-2
Yield, 120°C	105	--	MPa	ISO 527-2
Tensile Strain (Break)	3.0	--	%	ISO 527-2
Flexural Modulus (23°C)	8300	6200	MPa	ISO 178
Flexural Stress (23°C)	260	200	MPa	ISO 178
Coefficient of Friction				ASTM D3702
Dynamic	0.23	--		ASTM D3702
Static	0.18	--		ASTM D3702
Wear Factor	13.0	--		ASTM D3702

Thermal	Dry	Conditioned	Unit	Test Method
Coefficient of Linear Thermal Expansion	1.9E-5	--	cm/cm/°C	ISO 11359-2

Electrical	Dry	Conditioned	Unit	Test Method
Surface Resistivity	1.0E+13	--	ohms/sq	ASTM D257

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength (23°C)	19	--	kJ/m²	ISO 179
Charpy Unnotched Impact Strength (23°C)	65	--	kJ/m²	ISO 179

Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	255	--	°C	ISO 75-2/B
1.8 MPa, not annealed	253	--	°C	ISO 75-2/A
Thermal Conductivity	0.29	--	W/m/K	ISO 22007

Electrical	Dry	Conditioned	Unit	Test Method
Dielectric Strength (2.00 mm)	35	--	kV/mm	IEC 60243-1
Comparative Tracking Index	500	--	V	IEC 60112

Additional Information
干燥 The value listed as Molding Shrinkage ISO 294-4, was tested in accordance with S.O.P. methods.

Injection	Dry	Unit
Drying Temperature	100	°C
Drying Time	4.0	hr
Suggested Max Moisture	0.10	%
Rear Temperature	270 - 300	°C
Middle Temperature	270 - 300	°C
Front Temperature	285 - 300	°C
Nozzle Temperature	285 - 310	°C
Processing (Melt) Temp	< 300	°C
Mold Temperature	80 - 160	°C

Injection instructions
Pre-drying -- Since polyamides are hygroscopic materials as well as sensitive to moisture during processing, this product should always be pre-dried. At a humidity content above 0.1%, the material will begin to degrade. Recommended drying time is 4 hours at 100°C in dry-air dryer.Processing temperatures -- Melt temperature should be kept below 300°C in order to prevent degradation. The exact setting depends from machine and mold design, but is usually within the following range:Area \| RecommendationZone 1 (feed) 270-300°C \| 280°CZone 2 (middle) 270-300°C \| 290°CZone 3 (front) 285-300°C \| 295°CZone 4 (Nozzle) 285-310°C \| 300°CMold temperature -- The mold temperature is a compromise between the optimum properties that can be obtained from high crystallization, and cycle time. This material can be processed at mold temperatures between 80°C and 160°C. Optimum surface quality requires a mold temperature above 120°C.Regrind -- Regrind of highly filled thermoplastic materials, such as this material, should only be recycled with special care. The regrind content must never exceed 15%, and only regrind of optimum quality should be used. In any case, part properties should be checked.

Injection instructions

Pre-drying -- Since polyamides are hygroscopic materials as well as sensitive to moisture during processing, this product should always be pre-dried. At a humidity content above 0.1%, the material will begin to degrade. Recommended drying time is 4 hours at 100°C in dry-air dryer.Processing temperatures -- Melt temperature should be kept below 300°C in order to prevent degradation. The exact setting depends from machine and mold design, but is usually within the following range:Area | RecommendationZone 1 (feed) 270-300°C | 280°CZone 2 (middle) 270-300°C | 290°CZone 3 (front) 285-300°C | 295°CZone 4 (Nozzle) 285-310°C | 300°CMold temperature -- The mold temperature is a compromise between the optimum properties that can be obtained from high crystallization, and cycle time. This material can be processed at mold temperatures between 80°C and 160°C. Optimum surface quality requires a mold temperature above 120°C.Regrind -- Regrind of highly filled thermoplastic materials, such as this material, should only be recycled with special care. The regrind content must never exceed 15%, and only regrind of optimum quality should be used. In any case, part properties should be checked.

Category:	Nylon 66 , Polyamide 66
Manufacturer:	Solvay Specialty Polymers
Trademark:	Tribocomp®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	WkIQ82_TribocompPA66LGF30N9PTFE15MoS05.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Unichem 8530 BLACK	Colorite Polymers	PVC, Flexible	Unichem
Bakelite® MP 4165	Hexion Inc.	Mel Phenolic	Bakelite®
FRIANYL® A3 GF50 V0P1	Nilit Plastics	Nylon 66	FRIANYL®
ESTABLEND 7500 V0 HF	Cossa Polimeri S.r.l.	PC+ABS	ESTABLEND
TOTAL Polyethylene Lumicene® M 3583 UV (US)	TOTAL Refining & Chemicals	mMDPE	TOTAL Polyethylene