Order Products : sales@su-jiao.com
Vyncolit® GS431
| Category: | Phenolic , Phenolic |
| Manufacturer: | Vyncolit N.V. |
| Trademark: | Vyncolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WkEKPT_Vyncolit-GS431.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vyncolit GS431 is a cotton filled phenolic moulding compound with a high impact resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ISO 1183 |
| Apparent Density | 0.45 | g/cm³ | ISO 60 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.3 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 25.0 | MPa | ISO 527-2 |
| Flexural Modulus | 7750 | MPa | ISO 178 |
| Flexural Stress | 60.0 | MPa | ISO 178 |
| Compressive Stress | 160 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 6.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 6.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 150 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 15 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 125 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (4.00 mm) | V-1 | UL 94 |
| Additional Information |
|---|
| Apparent Density, ISO 60: 0.35 to 0.55 g/cm³Pourability: excellentMold Shrinkage, ISO 2577: 0.6 to 0.8 %Post Shrinkage, ISO 2577: 0.6 to 0.8 %Flexural Modulus, ISO 178: 7.0 to 8.5 GPaInsulation resistance dry, IEC 167: 0.8 G OhmInsulation resistance wet after 24 hours in water, IEC 167: 0.3 G Ohm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vipel® F701-FHG-00 | AOC, L.L.C. | Polyester Alloy | Vipel® |
| Witcom PS 2011/267 | Witcom Engineering Plastics B.V. | PS (GPPS) | Witcom PS |
| Baoding 67I98 | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU-Polyester | Baoding |
| Grivory® HT2C-3X black 9833 | EMS-GRIVORY | Nylon 6T/66 | Grivory® |
| 3M™ Dyneon™ PTFE Compound 310160003 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |