Chemlon® A82 Datasheet,Nylon 66,Teknor Apex Company (Chem Polymer)-SHANGHAI SUSHENG

Message
A82 is a UL recognised, V-0 rated halogen & phosphorus free flame retarded, unreinforced injection moulding grade of nylon 66.

General Information
Features	Phosphorus content, low (to none) Halogen-free Flame retardancy
Forms	Particle
Processing Method	Injection molding

Physical	Dry	Conditioned	Unit	Test Method
Density	1.19	--	g/cm³	ISO 1183
Molding Shrinkage ¹	1.0 - 1.5	--	%	Internal method
Water Absorption (Equilibrium, 23°C, 50% RH)	2.4	--	%	ISO 62

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus	3000	2800	MPa	ISO 527-2
Tensile Stress (Break)	70.0	55.0	MPa	ISO 527-2
Flexural Modulus	3300	1800	MPa	ISO 178
Flexural Stress ²	85.0	40.0	MPa	ISO 178

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength	7.0	35	kJ/m²	ISO 179

Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	> 220	> 220	°C	ISO 75-2/B
1.8 MPa, not annealed	110	99.0	°C	ISO 75-2/A

Electrical	Dry	Conditioned	Unit	Test Method
Surface Resistivity	1.0E+14	1.0E+11	ohms	IEC 60093
Volume Resistivity	1.0E+16	1.0E+14	ohms·cm	IEC 60093
Dielectric Strength (3.00 mm)	17	13	kV/mm	IEC 60243-1
Relative Permittivity	4.00	4.40		IEC 60250
Dissipation Factor (1 MHz)	0.020	0.080		IEC 60250
Comparative Tracking Index	> 600	> 600	V	IEC 60112

Flammability	Dry	Conditioned	Unit	Test Method
Flame Rating (0.570 mm)	V-0	--		UL 94
Glow Wire Flammability Index				IEC 60695-2-12
1.00 mm	960	--	°C	IEC 60695-2-12
1.50 mm	960	--	°C	IEC 60695-2-12
Glow Wire Ignition Temperature				IEC 60695-2-13
1.00 mm	960	--	°C	IEC 60695-2-13
1.50 mm	960	--	°C	IEC 60695-2-13
Oxygen Index	38	--	%	ISO 4589-2

Injection	Dry	Unit
Drying Temperature	80.0	°C
Drying Time	2.0	hr
Rear Temperature	270 - 290	°C
Middle Temperature	270 - 290	°C
Front Temperature	270 - 290	°C
Processing (Melt) Temp	< 300	°C
Mold Temperature	60.0 - 80.0	°C
Injection Rate	Fast
Screw Speed	50 - 200	rpm

Injection instructions
如果材料在空气中暴露的时间不超过3小时，则无需干燥。背压：低注射压力：高

Note Message
1 .	Mould shrinkage is significantly influenced by many factors including wall thickness, gating, moulding shape and processing conditions. The range values given are determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding).
2 .	At conventional deflection

Note Message

1 .

Mould shrinkage is significantly influenced by many factors including wall thickness, gating, moulding shape and processing conditions. The range values given are determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding).

2 .

At conventional deflection

Category:	Nylon 66 , Polyamide 66
Manufacturer:	Teknor Apex Company (Chem Polymer)
Trademark:	Chemlon®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	WidLtq_Chemlon-A82.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
APEX® 3600-80NT	Teknor Apex Company	PVC, Flexible	APEX®
Karina IVORY PVC COMPOUND 651D35/1-D-IS	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
LUVOCOM® 20-8332	Lehmann & Voss & Co.	PPA	LUVOCOM®
TOTAL Polypropylene PPR 12236	TOTAL Refining & Chemicals	PP Random Copolymer	TOTAL Polypropylene
LNP™ STAT-KON™ KE004 compound	SABIC Innovative Plastics	Acetal (POM) Copolymer	LNP™ STAT-KON™