SABIC® PPcompound 9120
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WhgXCP_SABIC-PPcompound-9120.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PPcompound 9120 is an elastomer-modified mineral filled Polypropylene with excellent impact and stiffness ratio. Typical material application are esthetical automotive interior parts. It has a very high scratch resistance, no stickiness and a high flow. SABIC® PPcompound 9120 is a designated automotive grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.990 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 21 | g/10 min | ISO 1133 |
| Molding Shrinkage (24 hr) | 0.85 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Injection Molded) | 65 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/1A/50 | ||
| Yield, Injection Molded | 21.0 | MPa | |
| Break, Injection Molded | 12.0 | MPa | |
| Tensile Strain (Break, Injection Molded) | 40 | % | ISO 527-2/1A/50 |
| Flexural Modulus 1(Injection Molded) | 1650 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | 20 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact Strength | ISO 180/4A | ||
| -20°C, Injection Molded | 4.0 | kJ/m² | |
| 0°C, Injection Molded | 7.0 | kJ/m² | |
| 23°C, Injection Molded | 20 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 110 | °C | ISO 75-2/B |
| CLTE - Flow | ASTM D696 | ||
| -30 to 30°C | 6.5E-5 | cm/cm/°C | |
| 23 to 80°C | 9.5E-5 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | Method I (3 point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RIALFILL CE 02 S 22 T0 | RIALTI Srl | PP Impact Copolymer | RIALFILL |
| SUPREME Specialty PS SP256 | Supreme Petrochem Ltd. | PS (Specialty) | SUPREME Specialty PS |
| Adell Polyamide BR-38 | Adell Plastics, Inc. | Nylon 6 | Adell Polyamide |
| LIHAN® B706BK | Nanjing Lihan Chemical Co., Ltd. | Nylon, Unspecified | LIHAN® |
| Jiangsu Meilan XXMLF3-12 | Jiangsu Meilan Chemical Co., Ltd. | Fluorelastomer | Jiangsu Meilan |