LNP™ THERMOCOMP™ GF004 compound
| Category: | PSU , Polysulfone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WhRgGs_LNP-THERMOCOMP-GF004-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP GF004 is a compound based on Polysulfone resin containing 20% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound GF-1004 Product reorder name: GF004 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.41 | g/cm³ | ASTM D792 |
| -- | 1.40 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.60 | % | ASTM D955 |
| Across Flow : 24 hr | 0.90 | % | ASTM D955 |
| Across Flow : 24 hr | 0.85 | % | ISO 294-4 |
| Flow : 24 hr | 0.64 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 6210 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 91.7 | MPa | |
| Break | 91.7 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield | 2.3 | % | |
| Break | 2.3 | % | |
| Flexural Modulus | |||
| -- | 6210 | MPa | ASTM D790 |
| -- | 6000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 138 | MPa | ASTM D790 |
| -- | 145 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 53 | J/m | ASTM D256 |
| 23°C 2 | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 430 | J/m | ASTM D4812 |
| 23°C 3 | 32 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 10.7 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 179 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 180 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 174 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 174 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 5.2E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 2.5E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 327 to 338 | °C | |
| Middle Temperature | 338 to 349 | °C | |
| Front Temperature | 349 to 360 | °C | |
| Processing (Melt) Temp | 360 to 371 | °C | |
| Mold Temperature | 149 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAZMID B 150 FV 07 | Mazzaferro Indústria e Comércio de Polímeros e Fibras Ltda. | Nylon 6 | MAZMID B |
| Ultraform® W 2320 U03 | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| LNP™ LUBRICOMP™ OFL36 compound | SABIC Innovative Plastics | PPS, Linear | LNP™ LUBRICOMP™ |
| SD POLYCA™ 875G20 | Sumika Styron Polycarbonate Limited | PC | SD POLYCA™ |
| TECACOMP® PEEK TRM XS black 4005 | Ensinger GmbH | PEEK | TECACOMP® |