Rilsan® BESN Noir P210 TL
| Category: | Nylon 11 , Polyamide 11 |
| Manufacturer: | Arkema |
| Trademark: | Rilsan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WhKbd1_Rilsan-BESN-Noir-P210-TL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rilsan ® BESN Noir P210 TL is a polyamide 11 produced from a renewable source. This black grade is plasticized and designed for extrusion. BESN Noir P210 TL falls into the PA11-PHLY category according to DIN 73378 and fulfils all specifications according to DIN 74324, ISO 7628, NFR 12632, and SAEJ844. MAIN APPLICATIONS
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 76 | ||
| Shore D, 15 sec | 67 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 600 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 32.0 | MPa | |
| Break | 54.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 31 | % | |
| Break | > 200 | % | |
| Flexural Modulus | 450 to 600 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 10.0 | mg | ISO 9352 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 10 | kJ/m² | |
| 23°C | 76 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 184 | °C | ISO 11357-3 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| ISO Shortname | PA11-HIP, EHL, 22-007 | ISO 1874 | |
| Renewable Carbon Conent | > 88 | % | ASTM D6866 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Melt Temperature | 230 to 280 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® RCopo 1.8.CL | Marco Polo International, Inc. | PP Random Copolymer | MARPOL® RCopo |
| Vyncolit® FS-4 | Vyncolit N.V. | DAP | Vyncolit® |
| ExxonMobil™ PP8244E1 | ExxonMobil Chemical | PP Impact Copolymer | ExxonMobil™ |
| Generic Polyester, TS - Glass\Mineral | Generic | Polyester, TS | Generic |
| Nylux 6/G33FL BLK | KMI Group, Inc. | Nylon 6 | Nylux |