WELLAMID Nylon 6600 CF 10 HWCP
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | CP-Polymer-Technik GmbH & Co. KG |
| Trademark: | WELLAMID Nylon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WgecVl_WELLAMID-Nylon-6600-CF-10-HWCP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
WELLAMID Nylon 6600 CF 10 HWCP is a Polyamide 66 (Nylon 66) material filled with 10% carbon fiber. It is available in Europe. Important attributes of WELLAMID Nylon 6600 CF 10 HWCP are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.19 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow : 4.00 mm | 0.90 | -- | % | |
| Flow : 4.00 mm | 0.40 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.2 to 2.7 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 12500 | 9000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 160 | 110 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.0 | 4.5 | % | ISO 527-2/5 |
| Flexural Modulus | 10500 | -- | MPa | DIN 52457 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | 14 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 35 | 65 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 250 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 250 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 230 | -- | °C | ISO 306/B50 |
| Melting Temperature | 255 | -- | °C | |
| CLTE - Flow (23 to 80°C) | 4.0E-5 | -- | cm/cm/°C | DIN 53752 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | < 1.0E+2 | -- | ohms | IEC 60093 |
| Volume Resistivity | < 50 | -- | ohms·cm | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | HB | -- | ||
| 3.20 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 275 to 295 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Riblene® FF 20 | Versalis S.p.A. | LDPE | Riblene® |
| WELLAMID Nylon 6600 GV 25 DHCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| NaturePlast PLI 012 | NaturePlast | PLA | NaturePlast |
| ASTAGLAS™ VH | Marplex Australia Pty. Ltd. | Acrylic (PMMA) | ASTAGLAS™ |
| Chemlon® 109-14 GH | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |