Ultramid® B3UG4
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WgKuGI_Ultramid-B3UG4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ultramid B3UG4 is a 20% glass reinforced, halogen free flame retardant injection molding PA6 grade with enhanced flammability protection and low smoke density. Resistant to glow wire test GWFI to 960 degrees Celsius |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.31 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 80.0 | -- | cm³/10min | ISO 1133 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 6000 | 3000 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 95.0 | 50.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 3.0 | 6.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 5700 | 2800 | MPa | ISO 178 |
| Flexural Stress (23°C) | 150 | 70.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 3.4 | -- | kJ/m² | |
| 23°C | 3.0 | 9.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | 35 | -- | kJ/m² | |
| 23°C | 40 | 110 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 210 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 170 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | -- | °C | ISO 3146 |
| RTI Elec | UL 746 | |||
| 0.710 mm | 65.0 | -- | °C | |
| 1.50 mm | 140 | -- | °C | |
| 3.00 mm | 140 | -- | °C | |
| RTI Imp | UL 746 | |||
| 0.710 mm | 65.0 | -- | °C | |
| 1.50 mm | 125 | -- | °C | |
| 3.00 mm | 125 | -- | °C | |
| RTI Str | UL 746 | |||
| 0.710 mm | 65.0 | -- | °C | |
| 1.50 mm | 140 | -- | °C | |
| 3.00 mm | 140 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Dielectric Constant (1 MHz) | 3.80 | -- | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.015 | -- | IEC 60250 | |
| Comparative Tracking Index | 550 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.710 mm | V-2 | -- | ||
| 1.50 mm | V-2 | -- | ||
| 3.00 mm | V-2 | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 250 to 275 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| StarTUFF TF 45-LR-9 | STAR Thermoplastic Alloys & Rubbers, Inc. | TPE | StarTUFF |
| Andur 93-AP | Anderson Development Company | PUR-Ether/TDI | Andur |
| Hylon® N1243THL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| INSPIRE™ 6021N | Braskem America Inc. | PP Homopolymer | INSPIRE™ |
| Hostacom TKC 451N D11449 | LyondellBasell Industries | PP Copolymer | Hostacom |