Generic PPE+PS - Glass Fiber, Milled
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WgKo1o_Generic-PPE-PS---Glass-Fiber-Milled.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PPE+PS - Glass Fiber, Milled This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.13 - 1.35 | g/cm³ | ASTM D792 |
| 23°C | 1.25 - 1.35 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/5.0 kg) | 8.5 - 49 | g/10 min | ASTM D1238 |
| Water Absorption (Saturation, 23°C) | 0.20 - 0.45 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 115 - 147 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 3100 - 4400 | MPa | ASTM D638 |
| 23°C | 3100 - 5000 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 59.0 - 75.0 | MPa | ASTM D638 |
| Yield, 23°C | 50.0 - 73.0 | MPa | ISO 527-2 |
| Fracture, 23°C | 57.0 - 75.0 | MPa | ASTM D638 |
| Fracture, 23°C | 50.0 - 73.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield, 23°C | 3.0 - 4.0 | % | ASTM D638, ISO 527-2 |
| Fracture, 23°C | 3.5 - 5.0 | % | ASTM D638 |
| Fracture, 23°C | 3.0 - 5.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 3200 - 4400 | MPa | ASTM D790 |
| 23°C | 3000 - 4700 | MPa | ISO 178 |
| Flexural Stress | |||
| 23°C | 95.0 - 123 | MPa | ISO 178 |
| Yield, 23°C | 100 - 120 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 30 - 40 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 35 - 55 | J/m | ASTM D256 |
| Unnotched Izod Impact Strength (23°C) | 25 - 35 | kJ/m² | ISO 180 |
| Instrumented Dart Impact (23°C) | 8.00 - 19.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 91.0 - 148 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 95.0 - 145 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 115 - 165 | °C | ASTM D1525 |
| -- | 110 - 167 | °C | ISO 306 |
| Linear thermal expansion coefficient | |||
| Flow | 4.5E-5 - 6.6E-5 | cm/cm/°C | ASTM E831 |
| Flow | 4.0E-5 - 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 4.8E-5 - 5.2E-5 | cm/cm/°C | ASTM E831 |
| Lateral | 5.0E-5 - 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity (23°C) | 0.28 - 0.29 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (23°C) | 15 - 33 | kV/mm | IEC 60243-1 |
| Relative Permittivity (23°C) | 3.05 | IEC 60250 | |
| Dissipation Factor (23°C) | 3.0E-3 - 6.0E-3 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 32 - 34 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 - 115 | °C | |
| Drying Time | 2.5 - 3.0 | hr | |
| Hopper Temperature | 70.0 - 90.0 | °C | |
| Rear Temperature | 250 - 280 | °C | |
| Middle Temperature | 270 - 300 | °C | |
| Front Temperature | 290 - 320 | °C | |
| Nozzle Temperature | 270 - 300 | °C | |
| Processing (Melt) Temp | 290 - 310 | °C | |
| Mold Temperature | 80.0 - 115 | °C |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PPE+PS - Glass Fiber, MilledThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Trithene® TS 7035 | Petroquimica Triunfo | LDPE | Trithene® |
| NORYL™ WCV072 resin | SABIC Innovative Plastics | PPE+PS+PP | NORYL™ |
| KumhoSunny PBT/ABS HAB8750 | Shanghai KumhoSunny Plastics Co., Ltd. | ABS+PBT | KumhoSunny PBT/ABS |
| MAJORIS EW367HM - 8229 | AD majoris | PP Copolymer | MAJORIS |
| POLYFORT® FPP 20 GFM HI | A. Schulman Europe | PP Homopolymer | POLYFORT® |