Order Products : sales@su-jiao.com
RTP 1205 T-70A
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WgBuiH_RTP-1205-T-70A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass Fiber Reinforced |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.10 - 0.30 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.40 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 10 sec) | 70 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 68.9 | MPa | ASTM D638 |
| Tensile Strength | 11.7 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 50 | % | ASTM D638 |
| Flexural Modulus | 138 | MPa | ASTM D790 |
| Flexural Strength | 5.17 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 210 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 210 | J/m | ASTM D4812 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | HB | UL 94 |
| Injection instructions |
|---|
| Desiccant Type Dryer Required. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POWERSIL® 600 A/B RED | Wacker Chemie AG | Silicone | POWERSIL® |
| HiFill® POM HO GF10 CC | Techmer Engineered Solutions | Acetal (POM) Homopolymer | HiFill® |
| KOPLA PA66 KDR1021 | KOPLA Co., Ltd. | Nylon 66 | KOPLA PA66 |
| KOPLA PP KPG1040 | KOPLA Co., Ltd. | PP, Unspecified | KOPLA PP |
| LUVOCOM® 1301-8675 | Lehmann & Voss & Co. | PPS | LUVOCOM® |