Quadrant EPP Duratron® XP (CM)
| Category: | Nylon, Unspecified , Polyamide |
| Manufacturer: | Quadrant Engineering Plastic Products |
| Trademark: | Quadrant EPP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Wfg7gv_Quadrant-EPP-Duratron-XP-CM-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Duratron XP is a compression-molded polyimide that offers high purity, high strength, high heat resistance, and good machinability. These properties, combined with its chemical resistance and dimensional stability, make Duratron XP ideal for components in semiconductor manufacturing and test equipment. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.40 | % | |
| Saturation | 1.3 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4020 | MPa | ASTM D638 |
| Tensile Strength (Ultimate) | 110 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 4140 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 138 | MPa | ASTM D790 |
| Compressive Modulus | 3100 | MPa | ASTM D695 |
| Compressive Strength (10% Strain) | 165 | MPa | ASTM D695 |
| Coefficient of Friction (vs. Steel - Static) | 0.23 | Internal Method | |
| Wear Factor | 100 | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 75 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 360 | °C | ASTM D648 |
| Maximum Use Temperature - Long Term, Air | 304 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Limiting Pressure Velocity 1 | 1.14 | MPa·m/s | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 323 | °C | ASTM D3418 |
| CLTE - Flow 2(-40 to 149°C) | 4.9E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity | 0.22 | W/m/K | ASTM F433 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 3 | > 1.0E+13 | ohms | Internal Method |
| Dielectric Strength 4 | 28 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.41 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 3.8E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.18 mm, Estimated Rating) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 4:1 safety factor |
| 2 . | 68°F |
| 3 . | EOS/ESD S11.11 |
| 4 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® HMN 6060 | Saudi Polymers Company | HDPE | Marlex® |
| Radilon® AGV 25 Natural | Radici Plastics | Nylon 66 | Radilon® |
| Caltex PP MT13 | GS Caltex | PP, Unspecified | Caltex PP |
| Thermec S™ 4150RC65 | Technical Polymers, LLC | PPS | Thermec S™ |
| LNP™ LUBRICOMP™ PFL38S compound | SABIC Innovative Plastics | Nylon 6 | LNP™ LUBRICOMP™ |