RTP 1309 C
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WeOrwd_RTP-1309-C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.76 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.15 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 123 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 16500 | MPa | ASTM D638 |
| Tensile Strength | 152 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 1.1 | % | ASTM D638 |
| Flexural Modulus | 15200 | MPa | ASTM D790 |
| Flexural Strength | 214 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 100 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 370 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 260 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.59 mm) | V-0 | UL 94 |
| Additional Information |
|---|
| The value listed as Flammability, UL 94, was tested in accordance with RTP test standards. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 6.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 302 - 343 | °C | |
| Middle Temperature | 302 - 343 | °C | |
| Front Temperature | 302 - 343 | °C | |
| Mold Temperature | 65.6 - 177 | °C | |
| Injection Pressure | 68.9 - 103 | MPa | |
| Clamp Tonnage | 6.9 - 11 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 283A HEC | RTP Company | Nylon 6 | RTP |
| Durethan® BKV 30 G H2.0 900051 | LANXESS Corporation | Nylon 6 | Durethan® |
| LOXIM 315 02 HB | LOXIM Industries Private Limited | Nylon 6 | LOXIM |
| OTECH TPE OW128W - Cable Jacket | OTECH Corporation | TPE | OTECH TPE |
| Sylvin 8925-70UV Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |