Moplen EP 400H
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Moplen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WdUlLb_Moplen-EP-400H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Moplen EP 400H is an heterophasic copolymer especially developed for extrusion applications. Moplen EP 400H exhibits high stiffness, very high impact properties at room and sub-zero temperatures, good dimensional stability and excellent creep and deforming resistance. The main applications of Moplen EP 400H are thermoforming, corrugated board and extrusion blow moulding. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.7 | g/10 min | ASTM D1238, ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 1.80 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 48.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1400 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield | 29.4 | MPa | ASTM D638 |
| Yield | 27.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 9.0 | % | ASTM D638 |
| Yield | 8.0 | % | ISO 527-2 |
| Break | > 50 | % | ISO 527-2 |
| Flexural Modulus | 1320 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -20°C | 7.0 | kJ/m² | ISO 179/1e |
| 0°C | 10 | kJ/m² | ISO 179/1e |
| 23°C | 30 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 190 | kJ/m² | |
| 0°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 78 | J/m | |
| 23°C | 740 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 78.0 | °C | ISO 75-2/B |
| Ductile / Brittle Transition Temperature | -55.0 | °C | ISO 6603-2 |
| Vicat Softening Temperature | |||
| -- | 153 | °C | ISO 306/A50 |
| -- | 70.0 | °C | ISO 306/B50 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (60°) | 65 | DIN 67530 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| polyvic® IM-1208-GL 06 | Unipack Plasindo | PVC, Semi-Rigid | polyvic® |
| SCHULATEC® PEEK WR 30 MV 14 | A. Schulman Europe | PEEK | SCHULATEC® |
| Sinvicomp SRP5610 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| TARFLON™ URZ2501 | Idemitsu Kosan Co., Ltd. | PC | TARFLON™ |
| IPC PP 4800HMH | International Polymers Corporation | PP Homopolymer | IPC PP |