Celstran® PA66-AF35-02-US
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celstran® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WdReX7_Celstran-PA66-AF35-02-US.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA66 with 35% aramid fiber by weight |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.30 | % | ASTM D955 |
| Transverse flow | 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 9030 | MPa | ASTM D638 |
| -- | 9200 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Fracture, 23°C | 119 | MPa | ASTM D638 |
| Fracture | 120 | MPa | ISO 527-2/1A/5 |
| Tensile Elongation | |||
| Fracture, 23°C | 1.6 | % | ASTM D638 |
| Fracture | 1.9 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 7800 | MPa | ISO 178 |
| Flexural Stress (23°C) | 180 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 15 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 246 | °C | ASTM D648, ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.18 | % | |
| Hopper Temperature | 70.0 - 80.0 | °C | |
| Rear Temperature | 285 - 295 | °C | |
| Middle Temperature | 290 - 300 | °C | |
| Front Temperature | 300 - 310 | °C | |
| Nozzle Temperature | 300 - 315 | °C | |
| Processing (Melt) Temp | 300 - 315 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Injection instructions |
|---|
| Zone 4 Temperature: 300 to 315°CFeed Temperature: 20 to 50°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TF1STT (Series: FC/S) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Evoprene™ 3274 | AlphaGary | SBS | Evoprene™ |
| Lucent PP TPP-230 | Lucent Polymers, Inc. | PP, Unspecified | Lucent PP |
| Hostacom HYS 2009R 105518 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| Durethan® BKV 30 H2.0 EF DUS029 901510 | LANXESS Corporation | Nylon 6 | Durethan® |